ALCOM® MS PC 1000 17115

Chemical Family: Polycarbonate (PC)

MOCOM Compounds ALCOM® MS PC 1000 17115 is a polycarbonate injection molding grade featuring low emission, easy release (demolding), heat stabilization and antisqueak-modified properties. It is mainly used for automotive interior decoration and finishing applications. Pre-drying conditions should be done in a dry air (dessiccant) dryer between 100-120°C for 2-3 hours, or in an air circulating dryer between 100-120°C for 4-12 hours, depending on the moisture content (max. moisture content should be < 0.02%). The suggested melt temperature is between 270-310°C and mold temperature between 80-110°C. Ensure that pre-drying is done properly to achieve optimal performance.

Product families

Applications

Automotive & Transportation — Automotive

Interior

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: ALCOM
Polymer Name: Polycarbonate (PC)
Additives Included: Anti-Squeak Agent, Heat Stabilizer
Anti-Squeak Agent
Heat Stabilizer
Processing Methods: Injection Molding
Markets: Automotive & Transportation
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Anti-Squeaking
Good Mold Release
Heat Stabilized
Low Emissions
Storage Condition: Store in dry, protected from light.
Pre-Drying Conditions: In an air circulatIng dryer 100-120 °C for 4-12 h; Dependant on moisture content; In a dry air (dessiccant) dryer 100-120 °C for 2-3 h
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Automotive Applications
Automotive Interior Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

8 rows

Characteristic	Value	Unit	Method
Tensile Modulus	2200.0	MPa	ISO 527
Tensile Stress at Yield	60.0	MPa	ISO 527
Tensile Elongation at Yield	6.0	%	ISO 527
Tensile Elongation at Break	85.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	no break	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	no break	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	65.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	19.0	kJ/m²	ISO 179/1eA

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Vicat B50	142.0	°C	ISO 306
HDT / A (1.8 MPa)	127.0	°C	ISO 75-1/-2

Table 3 of 5

1 row

Characteristic	Value	Unit
Moisture Content	max. 0.02	%

Table 4 of 5