ALCOM® PA6 900/1 GF5 GB25
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA6 900/1 GF5 GB25 is a heat-stabilized, low-warpage polyamide 6 base polymer with 5% glass fibers and 25% glass beads. It is used for injection-molded parts in the automotive and machinery market segments, such as housings. The processing injection-molding requirements are a melt temperature of 270-290°C and a mold temperature of 80-100°C. It should be stored in a light-proof container.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Bead, Glass Fiber
- Glass Bead
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Stabilized
- Low Warpage
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Housings
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 4600.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 2000.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 135.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 65.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 4900.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 2000.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 85.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.6 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 40.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 12.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 27.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 70.0 | kJ/m² | ISO 179/1eU |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1350.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 165.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 221.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.8 - 1 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.9 - 1.1 | % | ISO 294-4 |