ALCOM® PA6 900/1 PTFE10 IM
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA6 900/1 PTFE10 IM is a heat-stabilized, impact-modified, improved sliding/wear polyamide 6 with a 10% PTFE filler/additive system designed for functional components in the automotive and machinery markets. It should be pre-dried at 80°C in a dry air (dessiccant) dryer for 2-12 hours, depending on moisture content. Processing should be done through injection molding with a melt temperature of 270-290°C and a mold temperature of 80-100°C.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- PTFE
- Additives Included
- Heat Stabilizer, Impact Modifier
- Heat Stabilizer
- Impact Modifier
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Sliding Properties
- Heat Stabilized
- Impact Modified
- Improved Wear
- Wear Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 2200.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 800.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 68.0 | MPa | ISO 178 |
| Flexural Stress (Conditioned, 3.5% Strain) | 22.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 2400.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 850.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Dry) | 58.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Conditioned) | 35.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Dry) | 3.9 | % | ISO 527 |
| Tensile Elongation at Yield (Conditioned) | 20.0 | % | ISO 527 |
| Tensile Elongation at Break (Dry) | 15.0 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 100.0 | % | ISO 527 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1160.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 58.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.3 - 1.7 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.5 - 1.9 | % | ISO 294-4 |