ALCOM® PA6 900/8.4 GF10 MR20 BK0002-00
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA6 900/8.4 GF10 MR20 BK0002-00 is a heat-stabilized, easy-flow polyamide 6 with 10% glass fibers and 20% mineral filler/additive system. It is suitable for applications such as housings and functional components and can be processed by injection molding with a melt temperature of 270-290°C and mold temperature of 80-100°C. Prior to processing, the material should be pre-dried in a dry air (dessiccant) dryer at 80°C for 2-12 hours, depending on its moisture content.
Product families
Applications
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Heat Stabilized
- UV Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 7400.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 5800.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 170.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 120.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 8200.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 5500.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 110.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.6 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 65.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 6.5 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 40.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1370.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 200.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 1.5 mm) | HB | class | UL 94 |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |