ALCOM® MS PC+ABS 1000 17113
MOCOM Compounds ALCOM® MS PC+ABS 1000 17113 is a premium-grade engineering polymer specifically designed for injection molding applications in the automotive industry. This product is a blend of Polycarbonate and Acrylonitrile Butadiene Styrene (PC+ABS) and is modified with antisqueak additives to provide a comfortable and quiet driving experience.
Product families
Applications
Automotive & Transportation — Automotive
- Interior
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- ALCOM
- Density
- 1120.0 - 1120.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2300.0 - 2300.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Additives Included
- Anti-Squeak Agent
- Heat Stabilizer
- Material Features
- Anti-Squeaking
- Good Mold Release
- Heat Stabilized
- Low Emissions
- Storage Condition
Store in dry, protected from light tightly sealed.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-110 °C for 2-4 h; In an air circulatIng dryer 100-110 °C for 3-6 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Interior Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2300.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 70.0 | MPa | ISO 178 |
| Tensile Modulus | 2300.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 51.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 4.5 | % | ISO 527 |
| Tensile Elongation at Break | 35.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 235.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 47.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 15.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1120.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 121.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 111.0 | °C | ISO 75-1/-2 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 240 - 250 | °C |
| Mould Temperature | 70 - 100 | °C |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 17.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 260.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (24h) | 0.6 - 0.9 | % | ISO 294-4 |