ALCOM® LD2 PC 1000 UV 16104 WT2288-09TL
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALCOM® LD2 PC 1000 UV 16104 WT2288-09TL is a polycarbonate base polymer filled/additive system with UV stabilizers and light scattering special features for the Automotive and Lighting market segments. Its typical applications include lamp covers, display elements, and operating elements, and it has been approved by GS93016. Pre-drying conditions should be 120°C in a dry air (dessiccant) dryer for 2-4 hours and 120°C in an air circulating dryer for 4-12 hours with a maximum moisture content of <0.02%. Processing injection molding should be done at a melt temperature of 270-310°C and a mold temperature of 80-110°C.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Automotive Lighting
- Consumer Electronics
- Displays
Product Families
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Flexural Modulus
- 2300.0 - 2300.0 MPa
- Additives Included
- UV Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- OEM Standards
- BMW
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Light Diffusion
- Light Scattering
- Translucent
- UV Resistant
- UV Stabilized
- OEM Specifications
- BMW GS 93016
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- 120 °C in an air circulating dryer for 4-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Displays
- Lamp Covers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2300.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 76.0 | MPa | ISO 178 |
| Tensile Modulus | 2200.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 61.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 6.0 | % | ISO 527 |
| Tensile Elongation at Break | 100.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 13.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 11.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1190.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 146.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 128.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 310 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 7 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 16.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.6 - 0.9 | % | ISO 294-4 |