ALCOM® WP PC+ABS 5005 TFUV 16151
MOCOM Compounds ALCOM® WP PC+ABS 5005 TFUV 16151 is a polycarbonate + Acrylonitrile Butadiene Styrene blend with 5% PTFE and UV stabilization that has improved sliding and wear properties. It is used in automotive, machinery, and injection molded parts, such as housings, functional components, bearings, and sliding elements. Processing injection molding requires a melt temperature of 240-280°C and a mold temperature of 70-100°C.
Product families
Applications
- Housings & Enclosures
Product Families
- Blends & Alloys
Other characteristics
- Brand
- ALCOM
- Density
- 1200.0 - 1200.0 kg/m³
- End Uses
Automotive Applications, Bearings, Housings, Machine/Mechanical Parts, Sliding Parts
- Features
Good Sliding Properties, Improved Wear, UV Resistant, UV Stabilized, Wear Resistant
- Functions
- Resin
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2300.0 - 2300.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Fillers Included
- PTFE
- Additives Included
- UV Stabilizer
- Material Features
- Good Sliding Properties
- Improved Wear
- UV Resistant
- UV Stabilized
- Wear Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In an air circulatIng dryer 100-110 °C for 4-8 h; In a dry air (dessiccant) dryer 100-110 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Housings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2300.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 68.0 | MPa | ISO 178 |
| Tensile Modulus | 2200.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 47.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 4.2 | % | ISO 527 |
| Tensile Elongation at Break | 40.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 20.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 100.0 | MPa | ISO 2039-1 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1200.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 124.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 108.0 | °C | ISO 75-1/-2 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 240 - 280 | °C |
| Mould Temperature | 70 - 100 | °C |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 15.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 260.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (24h) | 0.6 - 0.9 | % | ISO 294-4 |