ALCOM® CFX ASA 5010 WP 16014 SV1019-16MC

Chemical Family: Styrenics

MOCOM Compounds ALCOM® CFX ASA 5010 WP 16014 SV1019-16MC is a pre-dried Acrylonitile/Styrene/Acrylate/Copolymer containing 10% PTFE with a metallic effect, improved sliding/wear and low tendency to flow lines. It is used in the machinery market segment for injection molded parts such as bearings and sliding elements. Pre-drying conditions include 80°C in a dry air (dessiccant) dryer for 2-4 hours, and 80°C in an air circulating dryer for 3-6 hours depending on the moisture content. The melt temperature for injection molding is 240-280°C and the mold temperature is 40-80°C. For optimal performance, it should be stored in a cool, dry, and dark place.

Product families

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: ALCOM
Polymer Name: Acrylonitrile Styrene Acrylate (ASA)
Fillers Included: PTFE
Processing Methods: Injection Molding
Markets: Industrial
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Good Sliding Properties
Improved Wear
UV Resistant
Storage Condition: Store in dry, protected from light.
Pre-Drying Conditions: 80 °C in a dry air (dessiccant) dryer for 2-4 h
80 °C in an air circulating dryer for 3-6 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Bearings
Machine/Mechanical Parts
Sliding Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

11 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2300.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	62.0	MPa	ISO 178
Tensile Modulus	2200.0	MPa	ISO 527
Tensile Stress at Yield	41.0	MPa	ISO 527
Tensile Elongation at Yield	2.7	%	ISO 527
Tensile Elongation at Break	15.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	50.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	35.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	6.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	2.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H358/30)	84.0	MPa	ISO 2039-1

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density	1140.0	kg/m³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Vicat B50	92.0	°C	ISO 306
HDT / A (1.8 MPa)	87.0	°C	ISO 75-1/-2

Table 4 of 5