To catalogue
ALCOM® AWL 10/3 WT1308-05LB
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
MOCOM Compounds ALCOM® AWL 10/3 WT1308-05LB is a base polymer of Acrylonitrile/Butadiene/Styrene/Copolymer that is opaque, highly reflective, heat stabilized, and has easy flow. It is suitable for markets such as Automotive and various application areas like lighting and light blocking components. Typical applications include light guides and reflectors.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Mineral
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Opacity
- Good Flow
- Good Light Reflection
- Heat Stabilized
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-4 h
- 80 °C in an air circulating dryer for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 60.0 | MPa | ISO 178 |
| Tensile Modulus | 2400.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 40.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 2.0 | % | ISO 527 |
| Tensile Elongation at Break | 8.8 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 48.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 110.0 | MPa | ISO 2039-1 |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1130.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 95.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 80.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 84.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.2 | % | ISO 13468 |
Table 6 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 220 - 260 | °C |
| Mould Temperature | 50 - 80 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 30.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |
| Shrinkage (24h) | 0.5 - 0.8 | % | ISO 294-4 |