ALCOM® PWL 10/1 WT1130-09LB
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALCOM® PWL 10/1 WT1130-09LB is a polycarbonate base polymer containing 15% special filler which is highly reflective and opaque and is impact modified. It is suitable for applications such as light guides and reflectors and can be used in the automotive and various market segments. For injection molding, a melt temperature of 280-320°C and a mold temperature of 80-110°C is recommended. Additionally, pre-drying conditions should include 120°C in a dry air (dessiccant) dryer for 2-4 hours, 120°C in an air circulating dryer for 4-12 hours, with a maximum moisture content of <0.02%.
Product families
Applications
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Functions
- Resin
- Polymer Name
- Polycarbonate (PC)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Mineral, Proprietary
- Mineral
- Proprietary
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Material Features
- Excellent Opacity
- Good Light Reflection
- High Reflectivity
- Impact Modified
- Light Blocking
- UV Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in an air circulating dryer for 4-12 h
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 77.0 | MPa | ISO 178 |
| Tensile Modulus | 2500.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 57.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 5.3 | % | ISO 527 |
| Tensile Elongation at Break | 60.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 18.0 | kJ/m² | ISO 179/1eA |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1320.0 | kg/m³ | ISO 1183 |
Table 3 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 142.0 | °C | ISO 306 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 80.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.1 | % | ISO 13468 |
Table 6 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (0.75 m) | HB | class | UL 94 |
| UL Recognition | yes | — | — |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 320 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 8.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.6 - 0.9 | % | ISO 294-4 |