ALCOM® PA66 910/1 GB30 MO2
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1 GB30 MO2 is a polyamide 66 base polymer with 30% glass beads and 2% molybdenium disulphide filler/additive system. It has improved sliding/wear, improved surface appearance, low warpage, and heat-stabilized features, and is mainly used in automotive and machinery applications such as bearings and sliding elements and functional components. Processing injection molding requires a melt temperature of 280-300°C and a mold temperature of 80-120°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Bead, Molybdenum Disulfide
- Glass Bead
- Molybdenum Disulfide
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Sliding Properties
- Good Surface Appearance
- Heat Stabilized
- Improved Wear
- Low Warpage
- Wear Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 4200.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 130.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 4500.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 80.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 3.1 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 20.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 2.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1360.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 92.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.9 - 1.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1 - 1.4 | % | ISO 294-4 |