ALCOM® PA66 910/1 GF15 MR25
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1 GF15 MR25 is a heat-stabilized polyamide 66 pre-dried with a dry air (dessiccant) dryer for 2-12 hours, depending on moisture content, with 15% glass fibers and 25% mineral filler/additive system. It has improved surface appearance, low warpage, and is suitable for housings and functional components. Processing is done via injection molding at a melt temperature of 280-300°C and a mold temperature of 80-120°C. For optimal performance, it should be stored in a dry, light-protected environment not exceeding 30°C and away from excessive heat and humidity.
Product families
Applications
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Surface Appearance
- Heat Stabilized
- Low Warpage
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 7800.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 190.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 8200.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 130.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.5 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 35.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1460.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 250.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.8 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 1 | % | ISO 294-4 |