ALCOM® PA66 910/1 PTFE20
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1 PTFE20 is a polyamide 66 base polymer with a 20% PTFE filler/additive system that provides improved sliding/wear properties. It is typically used for injection molded parts such as functional components, bearings, and sliding elements in the automotive and machinery market segments. Pre-drying conditions should be 80°C in a dry air (dessiccant) dryer for 2-12 h, depending on moisture content. For injection molding, melt temperatures should be 280-300°C and mold temperatures should be 80-120°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- PTFE
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Sliding Properties
- Good Tribological Properties
- Improved Wear
- Wear Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 2700.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 85.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 2900.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 65.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 6.3 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 70.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 55.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 3.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1250.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 70.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 260.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.4 - 1.8 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.8 - 2.2 | % | ISO 294-4 |