ALCOM® PA66 910/1.3 CF/GF30
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1.3 CF/GF30 is a polyamide 66 base polymer with 30% glass fiber/carbon fiber filler/additive system that is electrically conductive and heat stabilized with a high stiffness. It is suitable for various applications, such as bearings and functional components, in the automotive and machinery markets. For optimal results, it should be pre-dried at 80°C in a dry air (desiccant) dryer for 2-12 hours with a maximum moisture content of less than 0.15%.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
Carbon Fiber, Glass Fiber, Glass/Carbon Fiber, Milled Glass Fiber; Carbon Fiber; Glass Fiber; Glass/Carbon Fiber; Milled Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Electrically Conductive
- Heat Stabilized
- High Stiffness
- Reduced Surface Resistivity
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 10700.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 270.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 12000.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 195.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.7 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 35.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 6.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1330.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 252.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 262.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance (Conditioned) | max. 1000 | Ohm | IEC 62631-3-2 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.5 - 0.7 | % | ISO 294-4 |