ALCOM® AWL 109/10 GF20 WT1142-12LB
MOCOM Compounds ALCOM® AWL 109/10 GF20 WT1142-12LB is a base polymer of Acrylonitrile/Butadiene/Styrene/Copolymer, modified with polycarbonate and a Filler/Additive System of special filler, 20 % glass fibers. It features high reflectivity, opacity, heat stability, and stiffness, making it suitable for use in the Automotive and Lighting Market Segments for applications such as lighting, light blocking components, and light guides and reflectors. Processing Injection molding is done with a melt temperature of 240-270°C and a mold temperature of 60-100°C.
Product families
Applications
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
- Blends & Alloys
Other characteristics
- Brand
- ALCOM
- Density
- 1360.0 - 1360.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 6500.0 - 6500.0 MPa
- Tensile Strength
- 65.0 - 65.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Mineral
- Proprietary
- Additives Included
- Heat Stabilizer
- Material Features
- Excellent Opacity
- Good Light Reflection
- Heat Stabilized
- High Reflectivity
- High Stiffness
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-90 °C for 2-4 h; In an air circulatIng dryer 80-90 °C for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6500.0 | MPa | ISO 178 |
| Flexural Strength | 100.0 | MPa | ISO 178 |
| Tensile Modulus | 6800.0 | MPa | ISO 527 |
| Tensile Strength at Break | 65.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 17.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 145.0 | MPa | ISO 2039-1 |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1360.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 112.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 110.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 83.5 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.1 | % | ISO 13468 |
Table 6 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 240 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 8.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 240.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (24h) | 0.2 - 0.5 | % | ISO 294-4 |