ALCOM® MS PA66+6I/X 3050 17120
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® MS PA66+6I/X 3050 17120 is a high-performance engineering polymer that is designed for injection molding applications in the automotive and machinery market segments. This product is based on a partially aromatic polyamide and is reinforced with 50% glass fibers, which give it high stiffness and exceptional mechanical properties.
Product families
Applications
Automotive & Transportation — Automotive
- Interior
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66/6I/X
- Fillers Included
- Glass Bead, Glass Fiber
- Glass Bead
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Stabilized
- Low Anisotropic Shrinkage
- Superior Surface Quality
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Interior Parts
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 5800.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 4400.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 150.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 100.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 5800.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 4400.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 80.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.3 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 57.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 6.1 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 17.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 20.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1550.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 91.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 260.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.10 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.8 - 1 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |