To catalogue
Petkim PETILEN F2-26TO
- Chemical Family
- PolyethylenesPolyolefins
Petkim PETILEN F2-26TO is a low density polyethylene resin produced by high pressure tubular process. The product is developed for general purpose blown film applications used in packaging industry.
Product families
Applications
Building & Construction — Decorative Materials & Finishes
- Wallcoverings & Decorative Laminates
Printing & Packaging — Packaging
- Food & Beverage Packaging
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Polymer Name
- Low Density Polyethylene (LDPE)
- Melt Flow Index
- 2.5 - 2.5 g/10 min
- Additives Included
- Anti-Blocking Agent, Slip Agent
- Anti-Blocking Agent
- Slip Agent
- Processing Methods
- Extrusion, Film Extrusion
- Markets
- Building & Construction
- Printing & Packaging
- Storage
Inappropriate storage conditions can lead to bad smell, color changes and the deterioration in physical properties. It is advised to process PE resins within 6 months after delivery.
- PACKAGING
The material is packaged in PE bags or in PP big bags. The product should be stored in a dry area with an ambient temperature below 50°C. It should be kept away from sunlight, sparks, heat and flame.
- Recycling
The product is not hazardous or toxic and it is suitable for recycling using available recycling methods.
- Technology
- Plastics
- Labeling Claims
- Non-Hazardous
- Non-Toxic
- Recyclable
- Material Features
- Heat Stabilized
- Certifications and Compliance
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers End Uses
- Film
- Food Packaging
- Laminates
- Multilayer Film
- Plastics and Elastomers Functions
- Resin
- Recommended Processing Conditions
- Recommended Processing ConditionsFilm extrusion applications
- ;Typical zone temperature
- 140 - 180°C
- Typical melt temperature
- 160 - 180°C
- Typical blow-up ratio (BUR)
- 2:1 - 3:1
- Processing conditions should be optimized for different equipment design.
- Plastics and Elastomers Processing Methods
- Extrusion
- Film Extrusion
Technical data
Table 1 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Density, 23°C | 0.926 | g/cm³ | ASTM D1505 |
| Melting Point (DSC, 2nd heating) | 112 | °C | ASTM D3418 |
Table 2 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Point, 10 N | 92 | °C | ASTM D1525 |
Table 3 of 4
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield, MD | 12 | MPa | ASTM D882 |
| Tensile Strength at Yield, TD | 13 | MPa | ASTM D882 |
| Tensile Strength at Break, MD | 27 | MPa | ASTM D882 |
| Tensile Strength at Break, TD | 20 | MPa | ASTM D882 |
| Elongation at Break, MD | 150 | % | ASTM D882 |
| Elongation at Break, TD | 500 | % | ASTM D882 |
| Tear Strength, MD | 230 | cN | ASTM D1922 |
| Tear Strength, TD | 110 | cN | ASTM D1922 |
| Dart Drop Impact, F50 | 85 | g | ASTM D1709A |
| Coefficient of Friction | 0.2 | — | ASTM D1894 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Haze | 6.3 | % | ASTM D1003 |
| Gloss at 45° | 76 | GU | ASTM D2457 |