Petkim PETILEN YY F00756
- Chemical Family
- PolyethylenesPolyolefins
Petkim PETILEN YY F00756 is a high density polyethylene copolymer resin developed for blown film extrusion. The structure of the material is bimodal and it has broad molecular weight distribution. The product’s high stiffness makes it possible to produce very thin films.
Product families
Applications
- Industrial & Transport Packaging
Product Families
- Polyolefins
Other characteristics
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 0.07 - 0.07 g/10 min
- Processing Methods
- Blown Film Extrusion, Extrusion, Film Extrusion
- Markets
- Printing & Packaging
- Storage
Inappropriate storage conditions can lead to bad smell, color changes and the deterioration in physical properties. It is advised to process PE resins within 6 months after delivery
- PACKAGING
The material is packaged in PE bags or in PP Big Bags. The product should be stored in a dry area with an ambient temperature below 50°C. It should be kept away from sunlight, sparks, heat and flame
- Recycling
The product is not hazardous or toxic and it is suitable for recycling using available recycling methods
- Technology
- Plastics
- Labeling Claims
- Non-Hazardous
- Non-Toxic
- Recyclable
- Material Features
- Broad Molecular Weight Distribution
- High Stiffness
- Certifications and Compliance
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers End Uses
- Heavy Duty Bags
- Plastics and Elastomers Functions
- Resin
- Recommended Processing Conditions
Blown film extrusion applications;Typical zone temperatures: 200 - 260°CTypical blow-up ratio (BUR): 3:1 - 5:1Processing conditions should be optimized for different equipment design
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Extrusion
- Film Extrusion
Technical data
Table 1 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 24 | MPa | ASTM D638 |
| Tensile Strength at Break | 33 | MPa | ASTM D638 |
| Elongation at Break | 700 | % | ASTM D638 |
| Flexural Modulus, 23°C | 1000 | MPa | TS EN ISO 179 |
| Izod Impact Strength at 23°C (notched) | 225 | J/m | ASTM D256 |
| Hardness | 63 | Shore D | ASTM D2240 |
| Environmental Stress Crack Resistance (10% Igepal, F50) | min. 600 | h | ASTM D1693 |
Table 2 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (190°C/2.16 kg) | 0.07 | g/10 min | ASTM D1238 |
| Density, 23°C | 0.953 | g/cm³ | ASTM D1505 |
| Melting Point (DSC, 2nd heating) | 131 | °C | ASTM D3418 |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Point, 10 N | 123 | °C | ASTM D1526 |