Petkim PETILEN YY S0464
- Chemical Family
- PolyethylenesPolyolefins
Petkim PETILEN YY S0464 is a high density polyethylene resin having medium molecular weight distribution. The product is developed for medium size blow molding applications. The high flexural modulus of the material makes it possible to produce rigid goods.
Product families
Applications
- Consumer Goods — Apparel; Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications
- Textile Manufacturing
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
- Other Packaging Materials
Product Families
- Polyolefins
Other characteristics
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 0.36 - 0.36 g/10 min
- Processing Methods
- Blow Molding, Extrusion
- Markets
- Consumer Goods
- Industrial
- Printing & Packaging
- Storage
Inappropriate storage conditions can lead to bad smell, color changes and the deterioration in physical properties. It is advised to process PE resins within 6 months after delivery.
- PACKAGING
The material is packaged in PE bags or in PP Big Bags. The product should be stored in a dry area with an ambient temperature below 50°C. It should be kept away from sunlight, sparks, heat and flame.
- Recycling
The product is not hazardous or toxic and it is suitable for recycling using available recycling methods
- Technology
- Plastics
- Labeling Claims
- Non-Hazardous
- Non-Toxic
- Recyclable
- Material Features
- High Flexural Modulus
- Certifications and Compliance
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers End Uses
- Containers
- Cosmetic Packaging
- Film
- Flexible Packaging
- Fruit Juice Bottles
- Kitchenware
- Monofilaments
- Rigid Films
- Plastics and Elastomers Functions
- Resin
- Recommended Processing Conditions
Blow molding applications;Typical barrel temperature: 180 - 200°CTypical melt temperature: 190 - 210°CProcessing conditions should be optimized for different equipment design.
- Plastics and Elastomers Processing Methods
- Blow Molding
- Extrusion
Technical data
Table 1 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 28 | MPa | ASTM D638 |
| Tensile Strength at Break | 31 | MPa | ASTM D638 |
| Elongation at Break | 1115 | % | ASTM D638 |
| Flexural Modulus, 23°C | 1150 | MPa | TS EN ISO 181 |
| Izod Impact Strength at 23°C (notched) | 300 | J/m | ASTM D256 |
| Hardness | 65 | Shore D | ASTM D2240 |
| Environmental Stress Crack Resistance (10% Igepal, F50) | 16 | h | ASTM D1693 |
Table 2 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (190°C/2.16 kg) | 0.36 | g/10 min | ASTM D1238 |
| Density, 23°C | 0.961 | g/cm³ | ASTM D1505 |
| Melting Point (DSC, 2nd heating) | 134 | °C | ASTM D3418 |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Point, 10 N | 128 | g/10 min | ASTM D1525 |