SPINOPC® T43 001 GR08 2060
- Chemical Family
- Polycarbonate (PC)
SPINOPC® T43 001 GR08 2060 is a PC Unfilled Gray (RAL 7035) Flame Retardant for injection applications.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Furniture; Consumer Goods — Housewares; Agriculture & Feed — Other Agriculture & Feed Applications
Agriculture & Feed — Agricultural Films
- Other Agricultural Films
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
Building & Construction — Building Materials
- Structural Components
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Industrial — Leather & Textiles
- Textile Manufacturing
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- SPINOPC
- Polymer Name
- Polycarbonate (PC)
- Flexural Modulus
- 2200.0 - 2200.0 MPa
- Processing Methods
- Injection Molding
- Color
- Grey
- Markets
- Agriculture & Feed
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Material Features
- Chemical Resistant
- Excellent Mechanical Strength
- Flame Resistant
- Good Abrasion Resistance
- High Durability
- Impact Resistance
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Agricultural Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Cable Jacketing
- Connectors
- Construction Applications
- Electrical/Electronic Applications
- Furniture
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Young Modulus | 2350 | MPa | ISO 527-2 |
| Tensile Strength at Break | 65,0 | MPa | ISO 527-2 |
| Tensile Strength at Yield | 45,0 | Mpa | ISO 527-2 |
| Elongation at Break | min. 20 | % | ISO 527-2 |
| Elongation at Yield | 1,55 | % | ISO 527-2 |
| Flexural Modulus | 2200 | Mpa | ISO 178 |
| Flexural Strength | 80 | Mpa | ISO 178 |
| Charpy notched (23°C) | 10,0 | kJ/m2 | ISO 179 |
| Charpy notched (-30°C) | 8,0 | kJ/m2 | ISO 179 |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation in water 23°C) | 0,40 | % | ISO 62 |
| Water absorption,(Equilibrium value) (50% RH, 23°C) | 0,20 | % | ISO 62 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MFR/MFI(Melt Flow Rate) (190 °C 2,16 kg) | 13--18 | g / 10 min | ISO 1133 |
| VICAT (50 N - 50 °C/h) | 135 | °C | ISO 306 |
| HDT A (1.80 Mpa) | 120 | °C | ISO 75-2 |
| HDT B (0.45 Mpa) | 135 | °C | ISO 75-2 |
Table 4 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature, DSC | 105 - 145 | °C | ISO 11357-1/-3 |
| Melt Temperature, for processing | 220 - 240 | °C | — |
| Cylinder Settings | 220 - 260 | °C | — |
| Screw Design | Universal Type | — | — |
| Mould Temperature, injection moulding | 80 - 110 | °C | — |
| Moulding shrinkage (parallel,2mm) | 0,6 | % | ISO 294-4 |
| Moulding shrinkage (normal,2mm) | 0,6 | % | ISO 294-4 |
Table 5 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | VO | class | UL94 |
| GWFI(Glow Wire Flammability Index) (3 mm) | 960 | °C | IEC 60695 |
| GWIT (Glow Wire Ignitability Index) (2 mm) | 925 | °C | IEC 60695 |
| Comparative tracking index, CTI,(3mm-Solution A) | 225 | V | IEC 60112 |
| Volume Resistivity | 1.00E+15 | Ohm.m | IEC 60093 |
| Surface Resistivity | 10000000000000000 | ohm | IEC 60093 |