JURAPOM® X60 724 NC00 1000
- Chemical Family
- Waxes
JURAPOM® X60 724 NC00 1000 is a pom-c, 20% glass bead, natural (Heat stab.) for injection application.
Product families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- JURAPOM
- Polymer Name
- Polyacetal Homopolymer (POM)
- Flexural Modulus
- 4000.0 - 4000.0 MPa
- Technology
- Plastics
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2750 | MPa | ISO 527-2 |
| Young Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Strength at Break | 45 | MPa | ISO 527-2 |
| Tensile Strength at Yield | 25 | Mpa | ISO 527-2 |
| Elongation at Break | 30 | % | ISO 527-2 |
| Elongation at Yield | 1.55 | % | ISO 527-2 |
| Flexural Modulus | 4000 | Mpa | ISO 178 |
| Flexural Strength | 55 | Mpa | ISO 178 |
| Izod notched impact (23°C) | 5.5 | kJ/m2 | ISO 180/1A |
| Izod notched impact (-30°C) | 4.5 | kJ/m2 | ISO 180/1U |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.53 | g/cm3 | ISO 1183 |
| Ash Content | 20 | % | ISO 3451 |
| Water Absorption (Saturation in water 23°C) | 0.65 | % | ISO 62 |
| Water absorption,(Equilibrium value) (50% RH, 23°C) | 0.2 | % | ISO 62 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MFR/MFI(Melt Flow Rate,250 °C 2,16 kg) | 10-13 | g/10 min | ISO 1133 |
| VICAT (50 N - 50 °C/h) | 143 | °C | ISO 306 |
| HDT A (1.80 Mpa) | 90 | °C | ISO 75-2 |
| HDT B (0.45 Mpa) | 129 | °C | ISO 75-2 |
Table 4 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature, DSC | 165 | °C | ISO 11357-1/-3 |
| Melt Temperature, for processing | 190-200 | °C | — |
| Cylinder Settings | 180-210 | °C | — |
| Screw Design | Universal Type | — | — |
| Mould Temperature, injection moulding | 80-120 | °C | — |
| Moulding shrinkage (parallel,2mm) | 1.7 | % | ISO 294-4 |
| Moulding shrinkage (normal,2mm) | 1.7 | % | ISO 294-4 |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | class | UL94 |
| Comparative Tracking Index (CTI, 3 mm-Solution A) | 600 | V | IEC 60112 |
| Volume Resistivity | 1.00E+12 | Ohm.m | IEC 60093 |
| Surface Resistivity | 100000000000000 | ohm | IEC 60093 |