JURAPOM® X62 001 NC00 4023
- Chemical Family
- Waxes
JURAPOM® X62 001 NC00 4023 is a POM Unfilled Natural Wear Resistance for injection applications.
Product families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- JURAPOM
- Polymer Name
- Polyacetal Homopolymer (POM)
- Flexural Modulus
- 2150.0 - 2150.0 MPa
- Technology
- Plastics
Technical data
Table 1 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Young Modulus | 2000 | MPa | ISO 527-2 |
| Tensile Strength at Break | 45 | MPa | ISO 527-2 |
| Tensile Strength at Yield | 30 | Mpa | ISO 527-2 |
| Elongation at Break | min. 10 | % | ISO 527-2 |
| Elongation at Yield | 2,0 | % | ISO 527-2 |
| Flexural Modulus | 2150 | Mpa | ISO 178 |
| Flexural Strength | 70 | Mpa | ISO 178 |
| Charpy notched (23°C) | 6,0 | kJ/m2 | ISO 179 |
| Charpy notched (-30°C) | 5,5 | kJ/m2 | ISO 179 |
| Izod notched impact (23°C) | 4,5 | kJ/m2 | ISO 180/1A |
| Izod unnotched impact (-30°C) | 4,0 | kJ/m2 | ISO 180/1U |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation in water 23°C) | 0,60 | % | ISO 62 |
| Water absorption,(Equilibrium value) (50% RH, 23°C) | 0,18 | % | ISO 62 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MFR/MFI(Melt Flow Rate) (190 °C 2,16 kg) | 5 - 12 | g / 10 min | ISO 1133 |
| VICAT (50 N - 50 °C/h) | 145 | °C | ISO 306 |
| HDT A (1.80 Mpa) | 86 | °C | ISO 75-2 |
| HDT B (0.45 Mpa) | 126 | °C | ISO 75-2 |
| Coeff.of linear therm expansion | 13,0 | E-5/oC | ISO 11359 |
Table 4 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature, DSC | 165 | °C | ISO 11357-1/-3 |
| Melt Temperature, for processing | 180 - 210 | °C | — |
| Cylinder Settings | 180 - 230 | °C | — |
| Screw Design | Universal Type | — | — |
| Mould Temperature, injection moulding | 40 - 60 | °C | — |
| Moulding shrinkage (parallel,2mm) | 2,0 | % | ISO 294-4 |
| Moulding shrinkage (normal,2mm) | 2,0 | % | ISO 294-4 |
Table 5 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | class | UL94 |
| Volume Resistivity | 1.00E+14 | Ohm.m | IEC 60093 |
| Surface Resistivity | 10000000000000000 | ohm | IEC 60093 |