To catalogue
JURAPOM® X60 810 NC00
- Chemical Family
- Waxes
JURAPOM® X60 810 NC00 is a CO-POM Unfilled Impact Modifier Natural (Heat Stab.) for injection applications.
Product families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- JURAPOM
- Polymer Name
- Polyacetal Homopolymer (POM)
- Flexural Modulus
- 2250.0 - 2250.0 MPa
- Technology
- Plastics
Technical data
Table 1 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Young Modulus | 1750 | MPa | ISO 527-2 |
| Tensile Strength at Break | 50 | MPa | ISO 527-2 |
| Tensile Strength at Yield | 35 | Mpa | ISO 527-2 |
| Elongation at Break | min. 30 | % | ISO 527-2 |
| Elongation at Yield | 4,5 | % | ISO 527-2 |
| Flexural Modulus | 2250 | Mpa | ISO 178 |
| Flexural Strength | 65 | Mpa | ISO 178 |
| Charpy notched (23°C) | 12 | kJ/m2 | ISO 179 |
| Charpy notched (-30°C) | 8,0 | kJ/m2 | ISO 179 |
| Izod notched impact (23°C) | 14,0 | kJ/m2 | ISO 180/1A |
| Izod unnotched impact (-30°C) | 12,0 | kJ/m2 | ISO 180/1U |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation in water 23°C) | 0,80 | % | ISO 62 |
| Water absorption,(Equilibrium value) (50% RH, 23°C) | 0,25 | % | ISO 62 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MFR/MFI(Melt Flow Rate) (190 °C 2,16 kg) | 5 - 12 | g / 10 min | ISO 1133 |
| MVR(Melt Volume Rate) (190 °C 2,16 kg) | 4,5 - 10,5 | cm3/10 min | ISO 1133 |
| VICAT (50 N - 50 °C/h) | 126 | °C | ISO 306 |
| HDT A (1.80 Mpa) | 77 | °C | ISO 75-2 |
| HDT B (0.45 Mpa) | 135 | °C | ISO 75-2 |
Table 4 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature, DSC | 165 | °C | ISO 11357-1/-3 |
| Melt Temperature, for processing | 180 - 210 | °C | — |
| Cylinder Settings | 180 - 230 | °C | — |
| Screw Design | Universal Type | — | — |
| Mould Temperature, injection moulding | 40 - 60 | °C | — |
| Moulding shrinkage (parallel,2mm) | 1,80 | % | ISO 294-4 |
| Moulding shrinkage (normal,2mm) | 1,60 | % | ISO 294-4 |
Table 5 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | class | UL94 |
| Volume Resistivity | 1.00E+14 | Ohm.m | IEC 60093 |
| Surface Resistivity | 10000000000000000 | ohm | IEC 60093 |