To catalogue
MAGNAPBT® L60 007 NC00 1000
- Chemical Family
- Polyesters
MAGNAPBT® L60 007 NC00 1000 is a PBT 30% glass fiber natural heat aging for injection application.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Furniture; Consumer Goods — Housewares; Agriculture & Feed — Other Agriculture & Feed Applications
Agriculture & Feed — Agricultural Films
- Other Agricultural Films
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
Building & Construction — Building Materials
- Structural Components
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Industrial — Leather & Textiles
- Textile Manufacturing
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- MAGNAPBT
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 10500.0 - 10500.0 MPa
- Processing Methods
- Injection Molding
- Color
- Natural
- Markets
- Agriculture & Feed
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Material Features
- Chemical Resistant
- Excellent Long Term Heat Aging Properties
- Excellent Mechanical Strength
- Flame Resistant
- Good Abrasion Resistance
- High Durability
- Impact Resistance
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Agricultural Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Cable Jacketing
- Connectors
- Construction Applications
- Electrical/Electronic Applications
- Furniture
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2 |
| Young Modulus | 10000 | MPa | ISO 527-2 |
| Tensile Strength at Break | 135 | MPa | ISO 527-2 |
| Tensile Strength at Yield | 100 | Mpa | ISO 527-2 |
| Elongation at Break | 3 | % | ISO 527-2 |
| Elongation at Yield | 1.45 | % | ISO 527-2 |
| Flexural Modulus | 10500 | Mpa | ISO 178 |
| Flexural Strength | 165 | Mpa | ISO 178 |
| Charpy notched (23°C) | 12 | kJ/m2 | ISO 179 |
| Charpy unnotched (23°C) | 70 | kJ/m2 | ISO 179 |
| Izod notched impact (-30°C) | 11 | kJ/m2 | ISO 180/1A |
| Izod unnotched impact (23°C) | 9 | kJ/m2 | ISO 180/1A |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.53 | g/cm3 | ISO 1183 |
| Ash Content | 30 | % | ISO 3451 |
| Water Absorption (Saturation in water 23°C) | 0.2 | % | ISO 62 |
| Water absorption,(Equilibrium value) (50% RH, 23°C) | 0.4 | % | ISO 62 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MFR/MFI(Melt Flow Rate,250 °C 2,16 kg) | 40-50 | g/10 min | ISO 1133 |
| VICAT (50 N - 50 °C/h) | 215 | °C | ISO 306 |
| HDT A (1.80 Mpa) | 200 | °C | ISO 75-2 |
| HDT B (0.45 Mpa) | 220 | °C | ISO 75-2 |
Table 4 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature, DSC | 220 | °C | ISO 11357-1/-3 |
| Melt Temperature, for processing | 220-240 | °C | — |
| Cylinder Settings | 220-260 | °C | — |
| Screw Design | Universal Type | — | — |
| Mould Temperature, injection moulding | 60-100 | °C | — |
| Moulding shrinkage (parallel,2mm) | 0.3 | % | ISO 294-4 |
| Moulding shrinkage (normal,2mm) | 1.1 | % | ISO 294-4 |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | class | UL94 |
| Comparative Tracking Index (CTI, 3 mm-Solution A) | 500 | V | IEC 60112 |
| Volume Resistivity | 1.00E+14 | Ohm.m | IEC 60093 |
| Surface Resistivity | 1000000000000000 | ohm | IEC 60093 |