SPINOPC® P16-061
- Chemical Family
- Polycarbonate (PC)
SPINOPC® P16-061 is a PC 20% Glass Fiber Black for injection applications.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Furniture; Consumer Goods — Housewares; Agriculture & Feed — Other Agriculture & Feed Applications
Agriculture & Feed — Agricultural Films
- Other Agricultural Films
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
Building & Construction — Building Materials
- Structural Components
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Industrial — Leather & Textiles
- Textile Manufacturing
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- SPINOPC
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 5500.0 - 5500.0 MPa
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Agriculture & Feed
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Material Features
- Chemical Resistant
- Excellent Mechanical Strength
- Flame Resistant
- Good Abrasion Resistance
- High Durability
- Impact Resistance
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Agricultural Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Cable Jacketing
- Connectors
- Construction Applications
- Electrical/Electronic Applications
- Furniture
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 5400 | MPa | ISO 527-2 |
| Young Modulus | 6300 | MPa | ISO 527-2 |
| Tensile Strength at Break | 100 | MPa | ISO 527-2 |
| Tensile Strength at Yield | 90 | Mpa | ISO 527-2 |
| Elongation at Break | 3 | % | ISO 527-2 |
| Elongation at Yield | 1,7 | % | ISO 527-2 |
| Flexural Modulus | 5500 | Mpa | ISO 178 |
| Flexural Strength | 160 | Mpa | ISO 178 |
| Izod notched impact (23°C) | 7,5 | kJ/m2 | ISO 180/1A |
| Izod notched impact (-30°C) | 5,0 | kJ/m2 | ISO 180/1U |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Ash Content (750°C 30 min) | 20 | % | ISO 3451 |
| Water Absorption (Saturation in water 23°C) | 0,5 | % | ISO 62 |
| Water absorption,(Equilibrium value) (50% RH, 23°C) | 0,02 | % | ISO 62 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| VICAT (50 N - 50 °C/h) | 135 | °C | ISO 306 |
| HDT A (1.80 Mpa) | 135 | °C | ISO 75-2 |
| HDT B (0.45 Mpa) | 142 | °C | ISO 75-2 |
Table 4 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature, DSC | 145 | °C | ISO 11357-1/-3 |
| Melt Temperature, for processing | 220 - 240 | °C | — |
| Cylinder Settings | 260 - 280 | °C | — |
| Screw Design | Universal Type | — | — |
| Mould Temperature, injection moulding | 60 - 100 | °C | — |
| Moulding shrinkage (parallel,2mm) | 0,5 | % | ISO 294-4 |
| Moulding shrinkage (normal,2mm) | 0,7 | % | ISO 294-4 |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | class | UL94 |
| GWFI(Glow Wire Flammability Index) (3 mm) | 700 | °C | IEC 60695 |
| Comparative tracking index, CTI,(3mm-Solution A) | 400 | V | IEC 60112 |
| Volume Resistivity | 1.00E+14 | Ohm.m | IEC 60093 |
| Surface Resistivity | 10000000000000 | ohm | IEC 60093 |