CELLIDOR® CP 410-10

Chemical Family: Cellulose & Cellulosics

MOCOM Compounds CELLIDOR® CP 410-10 is a base polymer made of cellulose acetate propionate with a 10% phthalate-free plasticiser added as a filler/additive system. Pre-drying conditions involve an air circulating dryer at 60-90°C for 2-4 h, depending on the moisture content which should not exceed 0.15%. When processed via injection molding, the melt temperature should be between 180-230°C and the mold temperature should be between 40-80°C. Typical applications for this material include thick-walled parts with good strength and durability.

Product families

Plastics — Basic Thermoplastics

Cellulosics

Other characteristics

Brand: CELLIDOR
Density: 1210.0 - 1210.0 kg/m³
End Uses: Screw Driver Handles, Thick-Walled Parts
Polymer Name: Cellulose Acetate Propionate (CAP)
Additives Included: Plasticizer (Phthalate-free)
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Bio-based
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Non Phthalate Plasticizer
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In an air circulatIng dryer 60-90 °C for 2-4 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Screw Driver Handles
Thick-Walled Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Injection Molding

Technical data

Table 1 of 6

9 rows

Characteristic	Value	Unit	Method
Flexural Modulus	1800.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	45.0	MPa	ISO 178
Tensile Modulus	1800.0	MPa	ISO 527
Tensile Stress at Yield	43.0	MPa	ISO 527
Tensile Elongation at Yield	4.4	%	ISO 527
Tensile Elongation at Break	12.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	200.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	20.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H132/30)	95.0	MPa	ISO 2039-1

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1210.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Vicat B50	96.0	°C	ISO 306
HDT / A (1.8 MPa)	90.0	°C	ISO 75-1/-2