Aegis® H135MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It combines strength, toughness and exceptional thermoforming properties with excellent heat, chemical and abrasion resistance.
Properties
- Physical Form
- Pellets
Product families
- Polyamides
Other characteristics
- Brand
- Aegis®
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 2,690.0 MPa
- Additives Included
- Lubricant (Unspecified), Nucleating Agent
- Lubricant (Unspecified)
- Nucleating Agent
- Processing Methods
Blow Molding, Blown Film Extrusion, Extrusion, Film Extrusion, Thermoforming
- Markets
- Consumer Goods
- Food & Nutrition
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Abrasion Resistant
- Chemical Resistant
- Fast Crystallization
- Food Contact Acceptable
- Good Strength
- Heat Resistance
- High Viscosity
- Homopolymer
- Processing Guidelines
Aegis® H135MP homopolymer is supplied in sealed containers and drying prior to processing is not required. However, high moisture is the primary cause of processing problems. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level.
- Regulatory Compliance
AdvanSix has more than 50 years of experience in the development and production of packaging resin that is safe and reliable for consumers and businesses. Aegis® packaging resins are manufactured to meet the stringent standards required of materials involved in the processing, handling and packaging of food. They meet all applicable U.S. Food and Drug Administration (FDA) and European Union (EU) food grade regulations, as outlined in FDA 21 CFR 177.1500 and Regulation (EU) No. 10/2011.
- Certifications and Compliance
- EC Regulation 2011/10
- FDA 21 CFR 177.1500
- FDA 21 CFR Regulations
- FDA Compliant
- Plastics and Elastomers End Uses
- Balloons
- Book Covers
- Cast Films
- Film
- Flexible Packaging
- Food Packaging
- Form Fill Seal Packaging
- Pouches Flexible Packaging
Technical data
Table 1 of 3
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.13 | g/cm3 | ASTM D-792 |
| Extractable Content | max. 0.8 | % | SOP-702-307 |
| Melt Flow Rate (at 235°C/1.0 kg (455°F/1.0 kg)) | 1.2 | g/10min | ASTM D-1238 |
| Melting Point | 220 (428) | °C (°F) | ASTM D-3418 |
| Moisture (24 Hour) | 1.6 | % | ASTM D-570 |
| Moisture (50% RH) | 2.7 | % | ASTM D-570 |
| Moisture (Saturation) | 9.5 | % | ASTM D-570 |
| Moisture Content | max. 0.08 | % | ASTM D-6869 |
| RV (at 96% Sulfuric Acid) | 3.75 | — | — |
| Viscosity (FAV) | 135 | — | ASTM D-789 |
Table 2 of 3
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Carbon Dioxide Permeability | 72.8 | cc/m²/day | — |
| Elmendorf Tear Strength - MD (at 23°C (73°F)) | 840 | N | ASTM D-1922 |
| Elmendorf Tear Strength - TD (at 23°C (73°F)) | 1140 | N | ASTM D-1922 |
| Elongation - MD (at 23°C (73°F)) | 350 | % | ASTM D-882 |
| Elongation - TD (at 23°C (73°F)) | 360 | % | ASTM D-882 |
| Graves Tear - MD (at 23°C (73°F)) | 2540 | N | ASTM D-1004 |
| Graves Tear - TD (at 23°C (73°F)) | 2230 | N | ASTM D-1004 |
| Nitrogen Permeability | 14 | cc/m²/day | — |
| Oxygen Permeability (at 23°C (73°F)/0% RH) | 40.3 | cc/m²/day | D-3958 |
| Puncture Index - MD (at 23°C (73°F)) | 480 | gm/mil | ASTM D-5478 |
| Puncture Strength - MD (at 23°C (73°F)) | 940 | grams | ASTM D-5478 |
| Tensile Modulus - MD (at 23°C (73°F)) | 640 | MPa | ASTM D-882 |
Table 3 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus - MD (at 23°C (73°F)) | 2690 | MPa | ASTM D-790 |
| Flexural Strength - MD (at 23°C (73°F)) | 100 | MPa | ASTM D-790 |
| Heat Deflection Temperature - MD (at 23°C (73°F)) | 57 (135) | °C (°F) | ASTM D-648 |
| Notched Izod - MD (at 23°C (73°F)) | 60 | J/m | ASTM D-256 |
| Tensile Modulus - MD (at 23°C (73°F)) | 3130 | MPa | ASTM D-882 |
| Tensile Strength - MD (at 23°C (73°F)) | 80 | MPa | ASTM D-882 |
| Yield Elongation - MD (at 23°C (73°F)) | 3.7 | % | ASTM D-882 |