To catalogue
ForTii® Ace MX52
ForTii® Ace MX52 is a polyphthalamide (PPA) with unique fatigue performance and chemical resistance. Its high aromatic content and high Tg lead to excellent part stiffness and low creep, even at temperatures up to 150 °C. Moisture uptake occurs slowly, with minimal impact on dimensions. ForTii® Ace MX52 is processed using injection molding technology and is heat stabilized. It is 40% glass-reinforced and suitable for automotive applications.
Other characteristics
- Brand
- ForTii®
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding, Injection Molding
- Reinforcement Material
- Glass Fibers
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Key Benefits
Allowing a design without metal inserts; Highest creep resistance up to 140C; 10-20% Weight reduction; 10-30% Cost reduction; Potential of drop-in solution for existing heat shield design/tooling
- Technology
- Composite Materials
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Chemical Resistant
- Heat Stabilized
- High Stiffness
- High Strength
- Light Weight
- Reinforcement Form
- Tape
- Unidirectional Fabric
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Injection Molding
- Fan and Shrouds Application Data
- Faster injection molding process
- Holding step eliminated
- Shorter cooling time
- Lower weight
- Lower warpage
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Instrument Panel
- Carburetor Adapter Heat Shield Insulation Wall
- Cylinder Head Covers
- Door Panel
- Fans
- Flooring
- Front Spoiler
- Sunroof Frame Application Data
- Faster injection molding process
- Holding step eliminated
- Shorter cooling time
- Lower weight
- Lower warpage
- Plastics and Elastomers Functions
- Resin
- Instrument Panels Application Data
- Faster injection molding process
- Holding step eliminated
- Shorter cooling time
- Lower weight
- Lower warpage
- Application Data
- Faster injection molding process
- Holding step eliminated
- Shorter cooling time
- Lower weight
- Lower warpage
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
51 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 14500 / 15200 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 15000 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (40°C) | 14000 / 14000 | MPa | ISO 527-1/-2 |
| Tensile Modulus (80°C) | 13500 / 12300 | MPa | ISO 527-1/-2 |
| Tensile Modulus (100°C) | 13100 / 8100 | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 12800 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (150°C) | 9500 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 8000 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 6500 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 5900 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (210°C) | 5600 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 230 / 220 | MPa | ISO 527-1/-2 |
Table 2 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 335 / * | °C | ISO 11357-1/-3 |
| Glass Transition Temperature from DMTA (tan d) | 160 / * | °C | ASTM D5026/D7028 |
| Temperature of Deflection Under Load (1.80 MPa) | 320 / * | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 330 / * | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.17 / * | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.28 / * | E-4/°C | ASTM D696 |
| Coefficient of Linear Thermal Expansion (normal) | 0.54 / * | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.35 / * | E-4/°C | ASTM D696 |
| Thermal Index (2500 hrs) | 200 / * | °C | IEC 60216/ISO 527-1/-2 |
| Thermal Index (5000 hrs) | 189 / * | °C | IEC 60216/ISO 527-1/-2 |
| Thermal Index (10000 hrs) | 179 / * | °C | IEC 60216/ISO 527-1/-2 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 4 / * | % | Sim. to ISO 62 |
| Water Absorption in Water (at 23°C after 24h) | 0.32 / * | % | ISO 62 |
| Humidity Absorption | 1.7 / * | % | Sim. to ISO 62 |
| Density | 1550 / - | kg/m³ | ISO 1183 |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.35 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1 / * | % | ISO 294-4 |
| Spiral Flow Length 1.0 mm 1000 bar | 100 / * | mm | — |
Химическая стойкость
378 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | not resistant |
| Other | Acetic acid (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Other | Acetic anhydride | limited resistant, tests necessary to verify |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetonitrile | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | not resistant |
| Other | Acetylene at 23°C | resistant |