Arabian Chemical Industries GRIPWOOD
Arabian Chemical Industries GRIPWOOD is an one component solvent-free, liquid, resin-based high strength, insulating adhesive especiallyformulated for bonding wood of all types. It can also be used for bonding polystyrene and polyurethane insulationboard to concrete and other mineral substrates. It is WATERPROOF and has excellent moisture barrier properties.
Properties
- Physical Form
- Liquid
Product families
- Contact Adhesives
Other characteristics
- Product Type
- 1K (1 component) Adhesive, Contact Adhesive
- 1K (1 component) Adhesive
- Contact Adhesive
- Application Method
- Brush
- Compatible Substrates & Surfaces
- Wood
- Markets
- Building & Construction
- Packing
- GRIPWOOD is packed in 5 kg metal pail.
- Coverage
Approximately cover 31 to 47 square meters at 150 and 100 micronsrespectively.
- Advantages
Waterproof and permanently flexible. Especially suited in wet / high humidity areas such as bath rooms, sauna.; Superior adhesive strength.; High solids, solvent-free, ambient curing.; Wide range of service temperature (from -450C to +1750C). Suitable in sub floor heating system.; Flash (standby) time not required. Fast installation.; Interior and exterior applications.; One component, ready to use. Non-flammable.; Long open time, low odor.; Slightly foams to reduce the risk of gaps / hollow spots on uneven surface
- Appearance
- Liquid, dark brown color
- Shelf LIfe
One (1) year in original, unopened container stored in warehouse condition below 30° Celsius.. NOTE: after using, keep the container tightly closed, as the adhesive will harden when exposed to air.
- Technology
- Ready-to-Use Products
- Specification
GRIPWOOD Conforms with the most stringent requirement of BS EN 204 - Durability class D4, conditioning sequencenumber 6 (interior use with frequent long-term exposure to running or condensed water. Exterior use exposed toweather but with adequate protection by a surface coating).
- Packaging Type
- Pails
- Labeling Claims
- Non-Flammable
- Solvent-free
- Safety and Health
Always wear protective clothing, eye goggles, and rubber hand gloves when using. Avoid skin contact. Accidental spills to the skin should be washed immediately with soap and water. Accidental spills to the eyes should be washedimmediately with water. If irritation persists, consult a physician.. Always provide adequate air ventilation in the workplace. Avoid inhalation of vapors. May cause sensitization by inhalation and skin contact.
- Application Methods
- Brush
- Use Direction
Surface preparation - wood: must be clean and free from dirts, sealers, coatings, residual adhesives, etc. Surface must be plane and level. Lightlyabrade with emery paper. Finally, clean substrate with a cotton cloth moistened with clean water. Concrete / mineral substrates: must be clean and free from dirt, sealers, oil, laitance, curing compounds, etc.; Application - apply the adhesive using a palette knife or paint brush. Avoid excessive adhesive thickness. When bonding wood towood, it is advisable to apply the adhesive on both surfaces at a thickness of 100 microns. Press and or clamp thetwo surfaces for at least four (4) hours.; Cleaning - during installation, remove any excess adhesive from the surface with a cloth dampened with isokleen. Clean toolswith isokleen before adhesive cures.
Technical data
Table 1 of 1
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solids By Mass | 99.0 | % | — |
| Viscosity | 42.0 | poise | — |
| Elongation At Break | 40.0 | % | — |
| Open Time (35/25°C) | 45/90 | minutes. | — |
| Drying Time(Touch Dry,100Microns Wet Film On Glass At 25°C, 55 % Rh) | 4 - 5 | hours | — |
| Initial Drying Time(Hard, 100Microns Wet Film On Glass At 25°C, 55 % Rh) | 10.0 | hours | — |
| Final Drying Time(Hard, 100Microns Wet Film On Glass At 25°C, 55 % Rh) | 24.0 | hours | — |
| Tensile Shear Strength (Lap Joints) | 8.0 | N/sq.mm. | BS EN205 |