Turbo Lock Series 11 HT
- Chemical Family
- Esters
Turbo Lock Series 11 HT is a fast curing, removable, medium strength, high temperature, anaerobic thread-locking compound for bonding and sealing threads. It is highly resistance to heat, vibrations, water, gasses, oils, hydrocarbons and many chemicals. Disassembles with hand tools.
Product families
Applications
- Powertrain & UTH
- Construction Adhesives
- Fence Decks & Rails
- Industrial Adhesives & Sealants
- Industrial Manufacturing
Product Families
- Anaerobic Adhesives
Other characteristics
- Brand
- Turbo Lock
- Features
Chemical Resistant, Excellent Seal Properties, Fast Curing, Gas Barrier, Heat Resistance, High Temperature Resistance, Hydrocarbon Resistant, Medium Strength, Oil Resistant, Shock Resistant, Vibration Damping, Water Resistant
- Product Type
- Anaerobic Adhesive
- Application Area
- Transmission Applications
- Color
- Blue
- Markets
- Adhesives & Sealants
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 2 Years
- Precaution
This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
- Technology
- Ready-to-Use Products
- Application Methods
Surfaces should be dry, clean, and free of any contamination. Thread locker should be applied to the bolt in sufficient quantity to fill threads. Turbo-Lock 11-HT Series performs the best in thin bond gaps. This thread locker is specifically formulated to give controlled friction and torque/tension ratio during assembly.
- Storage Information
Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at a room temperature between 46°F to 82°F. Please do not return unused material to its original container.
- Ready to Use Product Features
- Chemical Resistant
- Excellent Seal Properties
- Fast Curing
- Gas Barrier
- Heat Resistance
- High Temperature Resistance
- Hydrocarbon Resistant
- Medium Strength
Technical data
Table 1 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion | 80x10⁻⁶ | K-1 | ASTM D 696 |
| Coefficient of Thermal Conductivity | 0.1 | W/(m.K) | ASTM C 177 |
| Specific Heat | 0.3 | kJ/(kg.K) | — |
Table 2 of 5
1 row| Characteristic | Value |
|---|---|
| Loctite® Equivalent | 246.0 |
Table 3 of 5
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Initial Strength Retained for Acetone (at 22ºC, 500hrs) | 95 | % |
| Initial Strength Retained for Ethanol (at 22ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Motor Oil (at 125ºC, 500hrs) | 95 | % |
| Initial Strength Retained for Gasoline (at 22ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs) | 90 | % |
| Initial Strength Retained for Acetone (at 22ºC, 1000hrs) | 90 | % |
| Initial Strength Retained for Ethanol (at 22ºC, 1000hrs) | 100 | % |
| Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs) | 95 | % |
| Initial Strength Retained for Gasoline (at 22ºC, 1000hrs) | 100 | % |
| Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs) | 100 | % |
| Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs) | 80 | % |
Table 4 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Handling Cure Time | 6 - 8 | minutes | — |
| Functional Cure Time | 1 - 3 | hrs | — |
| Full Cure Time | 24 | hrs | — |
| Breakaway Torque (M10 Steel Nuts and Bolts) | 18 (180) | N.m (lbs.in) | ISO 10964 |
| Prevail Torque (M10 Steel Nuts and Bolts) | 12 (48) | N.m (lbs.in) | ISO 10964 |
| Break Loose Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) | 15 - 24 (130 - 210) | N.m (lbs.in) | ISO 10964 |
| Maximum Prevail Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) | 4 - 9 (35 - 80) | N.m (lbs.in) | ISO 10964 |
| Temperature Range | -55 to 200 | ºC | — |
Table 5 of 5
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Color | Blue | — |
| Composition | Dimethacrylate ester | — |
| Viscosity (at 20 rpm, 25ºC, Brookfield RVT Spindle 3) | 2600 | cPs |
| Specific Gravity | 1.15 | — |
| Maximum Screw Size | ¾ (20) | inches (mm) |
| Flash Point | min. 100 | ºC |