Turbo Seal Series 65 Purple
- Chemical Family
- Methacrylates
Turbo Seal Series 65 Purple is a high performance anaerobic thread sealant designed for the locking and sealing of metal threaded pipes and fittings. The product cures quickly in the absence of air between close fitting surfaces and provides pressure resistance immediately after application. It is ideal to seal against gasses, water, LPG, hydrocarbons, oils and other chemicals. Excellent thixotropic property prevents migration of the sealant before and during curing.
Product families
Applications
- Pipes & Plumbing
Product Families
- Caulks & Sealants
Other characteristics
- Brand
- Turbo Seal
- Product Type
- Thread Sealant
- Application Area
- Pipes
- Color
- Purple
- Markets
- Building & Construction
- Precaution
This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
- Technology
- Ready-to-Use Products
- Use Direction
Surfaces should be dry, clean and free of any contamination. Apply 360° bead of product to the leading threads of the male fitting, leaving the first thread free. Force the material into the threads and voids, adjust product amount accordingly and apply a 360° bead of product on the female threads also. Assemble and tighten as required.
- Storage Information
Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at room temperature, 46°F to 82°F. Do not return unused material to its original container.
- Ready to Use Product Features
- Chemical Resistant
- Excellent Seal Properties
- Fast Curing
- Gas Barrier
- Good Sealant Properties
- High Performance
- Moisture Barrier
- Oil Resistant
Technical data
Table 1 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion | 80x10⁻⁶ | K-1 | ASTM D 696 |
| Coefficient of Thermal Conductivity | 0.1 | W/(m.K) | ASTM C 177 |
| Specific Heat | 0.3 | kJ/(kg.K) | — |
Table 2 of 5
2 rows| Characteristic | Value |
|---|---|
| Loctite® Equivalent | 545.0 |
| Permatex® Equivalent | 54550.0 |
Table 3 of 5
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Initial Strength Retained for Acetone (at 22ºC, 500hrs) | 95 | % |
| Initial Strength Retained for Ethanol (at 22ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Motor Oil (at 125ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Gasoline (at 22ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs) | 100 | % |
| Initial Strength Retained for Acetone (at 22ºC, 1000hrs) | 95 | % |
| Initial Strength Retained for Ethanol (at 22ºC, 1000hrs) | 90 | % |
| Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs) | 100 | % |
| Initial Strength Retained for Gasoline (at 22ºC, 1000hrs) | 95 | % |
| Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs) | 95 | % |
| Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs) | 100 | % |
Table 4 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Handling Cure Time | 10 - 30 | minutes | — |
| Functional Cure Time | 2 - 4 | hrs | — |
| Full Cure Time | 24 | hrs | — |
| Breakaway Torque (M10 Steel Nuts and Bolts) | 2 (20) | N.m (lbs.in) | ISO 10964 |
| Prevail Torque (M10 Steel Nuts and Bolts) | 2 (20) | N.m (lbs.in) | ISO 10964 |
| Break Loose Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) | 5 (44) | N.m (lbs.in) | ISO 10964 |
| Maximum Prevail Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) | 5 (44) | N.m (lbs.in) | ISO 10964 |
| Compressive Shear Strength of Steel Pins and Collars | min. 1.5 (220) | N/mm² (psi) | ISO 10123 |
| Operating Pressure | 10000 | psi | — |
| Temperature Range | -65 to 300 | ºF | — |
Table 5 of 5
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Composition | Methacrylate ester | — |
| Viscosity (at 20 rpm, 25ºC, Brookfield RVT Spindle 3) | 14000 | cPs |
| Specific Gravity | 1.2 | — |
| Flash Point | min. 100 | ºC |
| Solvent Content | None | — |