Palm Labs Adhesives Turbo Bond 300
- Chemical Family
- Methacrylates
Palm Labs Adhesives Turbo Bond 300 is a two-component, 100% reactive, toughened structural methacrylate adhesive specifically formulated for bonding wide variety of metals, thermoplastics, thermosets, and composite assemblies.
Product families
- Structural Adhesives
Other characteristics
- Product Type
- 2K (2 component) Adhesive, Reactive Adhesive
- 2K (2 component) Adhesive
- Reactive Adhesive
- Application Area
Furniture, Marine Applications, Metal Fabrication, Signage; Furniture; Marine Applications; Metal Fabrication; Signage
- Compatible Substrates & Surfaces
Aluminum, Composites, Fiberglass, Metal, Stainless Steel, Wood
- Color
- Black
- Curing
Working time is the approximate time, after mixing components A and B that the adhesive remains fluid and bondable. Fixture time is the approximate time after mixing components A and B required for the adhesive to develop sufficient strength to allow careful movement, unclamping or demolding of assembled parts. Parts can generally be put in service when 80 percent of full strength is developed. The time to achieve 80% cure is approximately 2-3 times that required for fixturing.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Clean Up
Adhesive components and mixed adhesive should be removed from mixing and application equipment with a suitable industrial solvent or cleaner before the mixed adhesive cures. Once the adhesive cures, soaking in a strong solvent or paint remover will be required to soften the adhesive for removal.
- Features
Convenient 1:1 mix ratio, Non-sagging and thixotropic formulation; Excellent impact, peel and shear resistance; Non-sagging, gaps filled up to 0.375 inches.; Room temperature cured with short open time.
- Appearance
- Milky white, Tan
- Technology
- Ready-to-Use Products
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity (at 25°C, Brookfield RVT) | 40,000 - 60,000 | cPs | — |
| Flash Point | 51 | °F | Tagliabue closed cup |
| Density | 8.55 | lbs/gal | — |
| Mix Ratio (Weight & Volume) | 1 | — | — |
Table 2 of 4
1 row| Characteristic | Value | Unit |
|---|---|---|
| Density | 8.71 | lbs/gal |
Table 3 of 4
2 rows| Characteristic | Value |
|---|---|
| Loctite® Equivalent | H3000 |
| Plexus® Equivalent | MA300 |
Table 4 of 4
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mixed Viscosity | 90,000 - 100,000 | cPs | — |
| Working Time | 4 - 6 | minutes | — |
| Fixture Time | 12 - 15 | minutes | — |
| Full Cure Time | 24 | hrs | — |
| Coverage/lb (at .010inch) | 148 | sq.in | — |
| Service Temperature | -40 to 250 | °F | — |
| Gap Filling (Adhesive) | max. 0.375 | inches | — |
| Shore-D Hardness (Adhesive) | 78 | — | ASTM D 2240 |
| Elongation of Adhesive | 19 | % | — |
| Tensile Shear Strength (Adhesive) | 4200 | psi | DIN 53283 |
| Impact Resistance (Adhesive) | 19 | ft.lb/in | — |