To catalogue
Turbo Fuse Series 115 SI
- Chemical Family
- Cyanoacrylates
Turbo Fuse Series 115 SI advanced formula is designed to polymerize instantly by absorbing surface moisture. The product's performance has been tested with a variety of materials, and is recommended for a multitude of applications. The fast curing qualities make it especially desirable in high speed industrial production. Turbo Fuse Series 115 SI is ideal for use in applications that require an easily handled low viscosity adhesive on difficult surfaces.
Product families
Applications
Building & Construction — Building Materials
- Pipes & Plumbing
Product Families
Ready-to-Use Products — Adhesives & Sealants
- Anaerobic Adhesives
Other characteristics
- Brand
- Turbo Fuse
- Features
Fast Curing, Good Wicking, High Performance, Low Viscosity
- Product Type
- 1K (1 component) Adhesive
- Compatible Substrates & Surfaces
Aluminum, Ceramic, Elastomers & Rubbers, Leather, Metal, Steel, Wood
- Color
- Transparent
- Markets
- Building & Construction
- Appearance
- Clear liquid, Clear hard (Cured)
- Shelf LIfe
- 1 Year
- Soluble In
- Acetone, MEK, Amide, Methylene Chloride
- Technology
- Ready-to-Use Products
- Quality Standards
- A-A-3097
- MIL-A-46050C
- Ready to Use Product Features
- Fast Curing
- Good Wicking
- High Performance
- Low Viscosity
- Compatible Substrates and Surfaces
- Aluminum
- Ceramic
- Elastomers & Rubbers
- Leather
- Metal
- Steel
- Wood
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Base Compound (Resin) | Surface insensitive ethyl cyanoacrylate | — | — |
| Viscosity | 20 | cPs | — |
| Flash Point | 160 - 200 | °F | Tagliabue closed cup |
Table 2 of 3
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shear Strength (Grit Based Steel) | min. 20 | N/mn² | ASTM D 1002/DIN 53283 |
| Shear Strength (Etched Aluminum) | min. 18 | N/mn² | ASTM D 1002/DIN 53283 |
| Shear Strength (Rubbers) | min. 22 | N/mn² | ASTM D 1002/DIN 53283 |
| Shear Strength (Wood) | min. 25 | N/mn² | ASTM D 1002/DIN 53283 |
| Shear Strength (Polycarbonate) | min. 12 | N/mn² | ASTM D 1002/DIN 53283 |
| Shear Strength (ABS) | min. 10 | N/mn² | ASTM D 1002/DIN 53283 |
| Average Set Time (Full Cure 24 hours, Metal) | 5 - 10 | seconds | — |
| Average Set Time (Full Cure 24 Hours, Plastic) | 5 - 10 | seconds | — |
| Average Set Time (Full Cure 24 Hours, Rubber) | 2 - 5 | seconds | — |
| Average Strength (Steel) | 22.0 | N/mm² | — |
| Loctite® Equivalent | 406.0 | — | — |
Table 3 of 3
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Full Cure Time | 24 | hrs |
| Melting Temperature | 160 - 170 | °C |
| Service Temperature | -65 to 80 | °C |
| Tensile Shear Strength | 18 - 28 | N/mm² |
| Gap Filling | 0.05 | mm |