Turbo Seal Series 50

Chemical Family: Esters

Turbo Seal Series 50 is an anaerobic gasket sealant, which develops medium strength in a short time. The compound cures in the absence of air between close fitting surfaces and will flex with minor flange movements. Provides resistance to low pressure immediately after assembly of flanges.

Properties

Physical Form: Gel

Product families

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Product Families

Ready-to-Use Products — Adhesives & Sealants

Anaerobic Adhesives

Other characteristics

Brand: Turbo Seal
Features: Chemical Resistant, Flexible, Gas Barrier, Good Compression Set, Good Strength, Hydrocarbon Resistant, Oil Resistant, Thixotropic, Water Resistant
Product Type: Anaerobic Adhesive
Application Area: Axle Covers, Compressors, Gaskets, Transmission Housing; Axle Covers; Compressors; Gaskets; Transmission Housing
Color: Purple
Markets: Industrial
Shelf LIfe: 1 Year
Precaution: This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
Technology: Ready-to-Use Products
Use Direction: For best results, clean all surfaces with a cleaning solvent and allow the solvent to evaporate; If the material is an inactive metal or the cure speed is too slow, spray with an Activator and allow to dry; Product is designed for flanged parts with gaps up to 0.25mm; Apply manually as a continuous bead or by screen-painting to one of surface flanges; Low pressure can be used when testing to confirm a complete seal immediately after assembly; Flanges should be tightened as soon as possible after assembly to avoid shimming
Storage Information: Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at a room temperature between 46°F to 86°F. Do not return unused material to its original container.
Ready to Use Product Features: Chemical Resistant
Flexible
Gas Barrier
Good Compression Set
Good Strength
Hydrocarbon Resistant
Oil Resistant
Thixotropic

Technical data

Table 1 of 5

3 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion	80x10⁻⁶	K-1	ASTM D 696
Coefficient of Thermal Conductivity	0.1	W/(m.K)	ASTM C 177
Specific Heat	0.3	kJ/(kg.K)	—

Table 2 of 5

5 rows

Characteristic	Value	Unit
Primed Average Cure Time	15 min. - 2 hrs	—
Unprimed Average Cure Time	1 - 12	hours
Loctite® Equivalent	515.0	—
Permabond® Equivalent	HH190	—
Permatex® Equivalent	51531.0	—

Table 3 of 5

12 rows

Characteristic	Value	Unit
Initial Strength Retained for Acetone (at 22ºC, 500hrs)	100	%
Initial Strength Retained for Ethanol (at 22ºC, 500hrs)	100	%
Initial Strength Retained for Motor Oil (at 125ºC, 500hrs)	100	%
Initial Strength Retained for Gasoline (at 22ºC, 500hrs)	100	%
Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs)	100	%
Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs)	90	%
Initial Strength Retained for Acetone (at 22ºC, 1000hrs)	95	%
Initial Strength Retained for Ethanol (at 22ºC, 1000hrs)	95	%
Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs)	100	%
Initial Strength Retained for Gasoline (at 22ºC, 1000hrs)	100	%
Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs)	100	%
Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs)	85	%

Table 4 of 5

8 rows

Characteristic	Value	Unit	Method
Handling Cure Time	15 - 90	minutes	—
Functional Cure Time	1 - 6	hrs	—
Full Cure Time	1 - 12	hrs	—
Shear Strength	4 - 9	N/mm²	ASTM D-1002
Tensile Strength	8 - 23	N/mm²	ASTM D-2095
Impact Strength	5 - 8	N/mm²	ASTM D-950
Elongation of Cured Film	min. 100	%	—
Temperature Range	-65 to 300	ºF	—

Table 5 of 5