epsotech PC CG1 NC
Epsotech PC CG1 NC is a single or multi-layer sheet with a glossy surface made of PC/ABS alloy.
Properties
- Physical Form
- Sheets
Product families
- Interior
Other characteristics
- Brand
- epsotech
- Density
- 1130.0 - 1130.0 kg/m³
- Features
Acid Resistant, Alkali Resistant, Freeze Resistant, Glossy Surface Aspects
- Polymer Name
- PC/ABS Alloy
- Notes
Unless otherwise stated, products are tested at a typical thickness of 4mm * The density quoted should only be used as a guide. This value can change depending upon the type and quantity of pigments or additives used. ** Fire behavior values given by raw material supplier or by indicative test on raw material. Not intended as a specification
- Drying
Space must be left between sheets to allow correct drying.
- Markets
- Automotive & Transportation
- Storage
Long storage times in humid conditions may require a product to be dried, e.g. 80oC for 2 hours +1hr per additional mm of thickness.
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Acid Resistant
- Alkali Resistant
- Freeze Resistant
- Glossy Surface Aspects
- Product Modification
Product code nomenclature takes in to account selected primary features of a product. The suffix may indicate a primary additional functionality, however, further multiple modifications are almost always possible and may be agreed upon and specified prior to our technical and commercial offer. Such enhancements are a normal part of our service capability and they do not affect the general characteristics listed in technical datasheets.
- Dimensional Tolerances
Standard tolerances are subject to the local standard tolerance set. Extra tolerance requirements may be possible on request and by special agreement
- Supplemental Information
Chemical Contact and cleaning Chemical resistance is influenced by many factors, including concentration, temperature, exposure time and material stress. Please contact our technical team for more information. Most common mild soaps dissolved in warm water can be used to effectively clean general dirt and surface contaminants, but in all cases should be objectively tested. Abrasive products will damage the surface.
- Plastics and Elastomers End Uses
- Automotive Interior Parts
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300.0 | MPa | ISO 527 |
| Yield Stress (23°C) | 50.0 | MPa | ISO 527 |
| Elongation at Break (23°C) | 50.0 | % | ISO 527 |
| Charpy (Notched, 23°C, 1eA) | 24.0 | KJ/m² | ISO 179 |
| Charpy (Notched, -30°C, 1eA) | 10.0 | KJ/m² | ISO 179 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density* | 1.13 | g/cm³ | ISO 1183 |
| UV Stabilisation (According to Customer Requirement) | Optional | — | — |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| VICAT Softening Point (B/50) | 118.0 | °C | ISO 306 |
| HDT-A (A 1.8MPa) | 102.0 | °C | ISO 75 |
Table 4 of 4
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Shrinkage | 0.5 - 0.7 | % |
| Thermoforming Temperature | 180 - 210 | °C |