BALTEK® SB.150
BALTEK® SB is a core material produced from select kiln-dried balsa wood in the ‘end-grain’ configuration. It has extremely high strength and stiffness to weight ratios, and achieves an excellent bond with all types of resins and adhesives. It is compatible with a variety of manufacturing processes and is resistant to temperature changes, or exposure to fire, or chemicals such as styrene. BALTEK® SB is an ideal core material for an extensive range of applications subjected to static or dynamic loads in service. All while being a renewable resource.
Product families
Applications
- Equipment & Parts
- Renewable Energy
- Aerospace & Aviation
- Marine
Product Families
- Wood Cores
Other characteristics
- Brand
- BALTEK
- End Uses
- Tanks
- Core Type
- Balsa Wood
- Functions
- Core Material
- Processing Methods
Prepreg Processing, Resin Transfer Molding (RTM), Spray Lay-up, Vacuum Infusion Processing (VIP)
- Markets
- Automotive & Transportation
- Industrial
- Core
- Balsa Wood
- Processing
- Adhesive bonding
- Compression molding
- Contact molding (hand/spray)
- Pre-preg processing (up to 180 °C, 355 °F)
- Resin injection (RTM)
- Vacuum infusion
- Application
- Marine
- Hulls, decks, bulkheads, superstructures, interiors, tooling/molds
- Road and Rail
- Floors, roofs, side skirts, front-ends, doors, interiors, covers
- Wind energy
- Rotor blades (shear webs and shells), nacelles, spinners
- Industrial
- Tanks, containers, architectural panels, impact limiters, sporting goods
- Aerospace
- Floors, cargo pallets, cargo containers, bulkheads, general aviation
- Defense
- Naval vessels, containers, cargo pallets, shelters, ballistic panels
- Technology
- Composite Materials
- Composites End Use
- Tanks
- Material Features
- Chemical Resistant
- Good Adhesion
- HIGHLIGHTS
Outstanding strength and stiffness to weight ratios; First-class, select grade lumber; Ecological product; Broadest range of available balsa densities worldwide; Certified for a range of applications by DNV, Germanischer Lloyd, Lloyd's Register, American Bureau of Shipping and Korean Register; Excellent fatigue and impact resistance; Fulfills most FST (flame, smoke, toxicity) requirements; Good sound and thermal insulation; Extremely wide operating temperature range (-212 °C to +163 °C (-414 °F to +325 °F)
- Composite Materials Functions
- Core Material
- Composites Processing Methods
- Prepreg Processing
- Resin Transfer Molding (RTM)
- Spray Lay-up
- Vacuum Infusion Processing (VIP)
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Apparent Nominal Density | 285 (17.8) | kg/m³ (lb/ft³) | ASTM C271 |
| Compressive Strength Perpendicular to the Plane | 22 (3184) | N/mm² (psi) | — |
| Compressive Modulus Perpendicular to the Plane | 4428 (642000) | N/mm² (psi) | — |
| Tensile Strength Perpendicular to the Plane (Polyester) | 12.2 (1770) | N/mm² (psi) | — |
| Tensile Strength Perpendicular to the Plane (Polyester) | 18.3 (2654) | N/mm² (psi) | — |
| Tensile Modulus Perpendicular to the Plane | 6604 (957600) | N/mm² (psi) | — |
| Shear Strength | 5.2 (761) | N/mm² (psi) | — |
| Shear Modulus | 362 (52600) | N/mm² (psi) | — |
| ContourKore Thickness (CK) | 6 to 50 (¼ to 2) | mm +0.25 -0.75 (in +0.01 -0.03) | — |
| Minimum Sheet Density | 248 (15.5) | kg/m³ (lb/ft³) | ASTM C271 |
Table 2 of 2
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Standard Sheet Width | 610 (24) | mm ± 5 (in ± 3/16) |
| Standard Sheet Length | 1220 (48) | mm ± 10 (in ± 3/8) |
| Thermal Conductivity at Room Temperature | 0.084 (0.581) | W/m.K (BTU.in/ft2.hr.°F) |
| Standard Sheet Thickness | 6 to 76 (¼ to 3) | mm +0.25 -0.75 (in +0.01 -0.03) |