AIREX® T92.60
AIREX® T92 is a closed-cell, thermoplastic and recyclable polymer foam with very good mechanical properties and an outstanding price / performance ratio. It has an extraordinary resistance to fatigue, is chemically stable and has negligible water absorption. It is thermally stable during high temperature processing and post curing without after expansion or out-gassing. T92 is designed for easy use with all resin systems and processing technologies. AIREX® T92 is ideally suited as a core material for a wide variety of lightweight sandwich structures subjected to static and dynamic loads and/or exposed to elevated temperatures during manufacturing
Product families
Applications
- Exterior & Body
- Renewable Energy
- Marine
Product Families
- Foam Cores
Other characteristics
- Brand
- AIREX
- Core Type
- Thermoplastic Foam
- Functions
- Core Material
- Markets
- Automotive & Transportation
- Industrial
- Core
- Thermoplastic Foam
- Processing
- Contact molding (hand/spray)
- Vacuum infusion
- Resin infusion / injection (VARTM / RTM)
- Adhesive bonding
- Pre-preg processing
- Compression molding (GMT, SMC)
- Thermoforming
- Application
- Wind energy
- Blades (shear webs & shells), nacelles
- Marine
- Decks, hull sides, superstructures, bulkheads, transoms, interiors
- Industrial
- Covers, containers, local reinforcements, x-ray tables, sporting goods
- Transportation
- Truck body parts, floors
- Technology
- Composite Materials
- Material Features
- Flame Retardant
- HIGHLIGHTS
Easy to process with all types of resin and lamination processes; High process temperature up to 150 °C (302 °F); Outstanding fatigue strength; Best-in-class resin uptake; Very high chemical stability; Good adhesion (skin-to-core bond); Excellent long term thermal stability up to 100 °C (212 °F); No water absorption, after expansion nor out-gassing; Recyclable and recycled material; Highly consistent material properties; Comprehensive material traceability (machine-readable batch information on each foam sheet)
- Composite Materials Functions
- Core Material
- Composites Processing Methods
- Compression Molding
- Prepreg Processing
- Spray Lay-up
- Thermoforming
- Vacuum Infusion Processing (VIP)
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Tensile Strength Perpendicular to the Plane | 1.5 (218) | N/mm² (psi) |
| Shear Elongation at Break | 25.0 | % |
| Compressive Strength Perpendicular to the Plane | 0.85 (123) | N/mm² (psi) |
| Compressive Modulus Perpendicular to the Plane | 55 (7‘980) | N/mm² (psi) |
| Tensile Modulus Perpendicular to the Plane | 85 (12‘330) | N/mm² (psi) |
| Shear Strength | 0.55 (80) | N/mm² (psi) |
| Shear Modulus Parallel to welding lines | 15 (2‘180) | N/mm² (psi) |
| Shear Modulus Across welding lines | 14 (2‘030) | N/mm² (psi) |
| Shear Modulus Across welding lines | 12 (1‘740) | N/mm² (psi) |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Standard Sheet Length | 2440 (96) | mm ± 5 (in ± 0.2) |
| Density | 65 (4.1) | kg/m³ (lb/ft³) |
| Thermal Conductivity at 10°C | 0.037 (0.257) | W/m.K (BTU.in/ft2.hr.°F) |
| Standard Sheet Width | 1220 (48) | mm ± 5 (in ± 0.2) |
| Standard Sheet Thickness | 5 to 100 (⅛ to 4) | mm ± 0.5 (in ± 0.02) |