ALCOM® MED PS 1000 AS 14114

Chemical Family: Styrenics

MOCOM Compounds ALCOM® MED PS 1000 AS 14114 is a polystyrene impact resin with a permanent antistatic filler/additive system designed for Medical/Personal Care applications, suitable for injection molded parts such as housings. Its melt temperature should be between 180-260°C and its mold temperature should be between 10-70°C. Pre-drying should be done in an air circulating dryer at 60-80°C for 2-3 hours, or in a dry air (dessicant) dryer at 60-80°C for 2-3 hours, depending on the moisture content.

Product families

Applications

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: ALCOM® MED
Polymer Name: Polystyrene (unspecified)
Additives Included: Anti-Static Agent
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Shelf LIfe: Minimum 24 months
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Anti-Static
High Impact Performance
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In a dry air (dessiccant) dryer 60-80 °C for 2-3 h; In an air circulatIng dryer 60-80 °C for 2-3 h; Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Housings
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

10 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2300.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	40.0	MPa	ISO 178
Tensile Modulus	2200.0	MPa	ISO 527
Tensile Stress at Yield	26.0	MPa	ISO 527
Tensile Elongation at Yield	1.3	%	ISO 527
Tensile Elongation at Break	12.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	30.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	24.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	5.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	2.0	kJ/m²	ISO 179/1eA

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density	1040.0	kg/m³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Vicat B50	81.0	°C	ISO 306
HDT / A (1.8 MPa)	69.0	°C	ISO 75-1/-2

Table 4 of 5