TECACOMP PPS CF30 TF15 black 1061041
- Chemical Family
- Polyphenylene Sulfide (PPS)Polysulfides
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- TECACOMP
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Carbon Fiber, PTFE
- Carbon Fiber
- PTFE
- Processing Methods
- Injection Molding
- Color
- Black
- Predrying
To achieve optimum mechanical properties, it is recommended to pre-dry the material w ith the above mentioned parameters.
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Processing Information
This material can be processed as a thermoplastic taking the normal technical provisions into account. The above mentioned information refers exclusively to the injection molding process.. Processing should be carried out as gently as possible, in order to maintain the maximum fiber length in the component. Back pressure and injection rate should be adjusted to the component geometry accordingly. The optimum processing temperature depends upon the respective geometry of the molded part and can be different from machine to machine.
- Certifications and Compliance
- UL 94
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength | 25 | kJ/m2 | DIN EN ISO 179-1eU |
| Elongation at Break | 0.7 | % | DIN EN ISO 527-1 |
| Modulus of Elasticity (Tensile test) | 27000 | MPa | DIN EN ISO 527-1 |
| Tensile Strength | 160 | MPa | DIN EN ISO 527-1 |
Table 2 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Density | 1.52 | g/cm3 |
Table 3 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glass Transition Temperature | 90 | °C | DIN 53765 |
| Glass Transition Temperature | 277 | °C | ISO-R 75 Method A |
| Melting Temperature | 280 | °C | DIN 53765 |
| Service Temperature (long term) | 230 | °C | — |
| Service Temperature (short term) | 260 | °C | — |
| Thermal Conductivity (in-plane) | 1.21 | W/(K*m) | DIN EN 821 |
| Thermal Conductivity (through-plane) | 0.46 | W/(K*m) | DIN EN 821 |
| Thermal Expansion (CLTE) Longitudinal (at 130 - 220°C) | 19 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Thermal Expansion (CLTE) Longitudinal (at 23 - 80°C) | 7 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Thermal Expansion (CLTE) Transverse (at 130 - 220°C) | 63 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Thermal Expansion (CLTE) Transverse (at 23 - 80°C) | 28 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Electrical Conductivity | 9 x 10^3 | S/m | DIN EN ISO 3915 |
Table 5 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bulk Density | 0.56 | g/cm3 | EN ISO 60 |
| Flammability (UL94 at 1.6 and 3.2 mm) | V0 | % | — |
| Melt Flow Index (316°C / 2.16 kg) | 6 | g/10 min | DIN EN ISO 1133 |
| Molding Shrinkage (in-plane) | 0.23 | % | DIN EN ISO 294-4 |
| Molding Shrinkage (through-plane) | 0.51 | % | DIN EN ISO 294-4 |
| Water Absorption (50 % rel. H. 24 h) | 0.006 | % | DIN EN ISO 62 |