TECACOMP PEEK 450 ID blue 3865
- Chemical Family
- Polyether Ether Ketone (PEEK)
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Housewares
Electrical & Electronics — Packaging & Assembly
- Other Packaging & Assembly Applications
Food & Nutrition — Processing & Packaging
- Food & Beverage Manufacturing
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- TECACOMP
- Polymer Name
- Polyetheretherketone (PEEK)
- Fillers Included
- Other Filler
- Processing Methods
- Injection Molding
- Color
- Blue
- Markets
- Consumer Goods
- Electrical & Electronics
- Food & Nutrition
- Predrying
To achieve optimum mechanical properties, it is recommended to pre-dry the material w ith the above mentioned parameters.
- Technology
- Plastics
- Material Features
- Metal Detectable
- Processing Information
This material can be processed as a thermoplastic taking the normal technical provisions into account. The above mentioned information refers exclusively to the injection molding process.. Processing should be carried out as gently as possible, in order to maintain the maximum fiber length in the component. Back pressure and injection rate should be adjusted to the component geometry accordingly. The optimum processing temperature depends upon the respective geometry of the molded part and can be different from machine to machine.
- Certifications and Compliance
- FDA Compliant
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers End Uses
- Cable Ties
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength | n.B. | kJ/m2 | DIN EN ISO 179-1eU |
| Elongation at Break (50 mm/min) | 14 | % | DIN EN ISO 527-1 |
| Elongation at Yield | 4.5 | % | DIN EN ISO 527-1 |
| Modulus of Elasticity (Tensile test, 50 mm/min) | 4300 | MPa | DIN EN ISO 527-1 |
| Tensile Strength (50 mm/min) | 96 | MPa | DIN EN ISO 527-1 |
| Tensile Strength at Break | 80 | MPa | DIN EN ISO 527-1 |
| Tensile Strength at Yield | 96 | MPa | DIN EN ISO 527-1 |
Table 2 of 4
1 row| Characteristic | Value | Unit |
|---|---|---|
| Density | 1.44 | g/cm3 |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glass Transition Temperature | 143 | °C | DIN 53765 |
| Melting Temperature | 343 | °C | DIN 53765 |
| Service Temperature (long term) | 260 | °C | — |
| Service Temperature (short term) | 300 | °C | — |
Table 4 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bulk Density | 0.8 | g/cm3 | EN ISO 60 |
| Detectability | 3.7 | mm Al | — |
| Melt Flow Index | 7 | g/10 min | DIN EN ISO 1133 |