TECACOMP PEEK TC black 1054135
- Chemical Family
- Polyether Ether Ketone (PEEK)
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Automotive Lighting
Electrical & Electronics — Devices & Assemblies
- Lighting
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- TECACOMP
- Polymer Name
- Polyetheretherketone (PEEK)
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Predrying
To achieve optimum mechanical properties, it is recommended to pre-dry the material w ith the above mentioned parameters.
- Technology
- Plastics
- Processing Information
This material can be processed as a thermoplastic taking the normal technical provisions into account. The above mentioned information refers exclusively to the injection molding process.. Processing should be carried out as gently as possible, in order to maintain the maximum fiber length in the component. Back pressure and injection rate should be adjusted to the component geometry accordingly. The optimum processing temperature depends upon the respective geometry of the molded part and can be different from machine to machine.
- Plastics and Elastomers End Uses
- Lighting Applications
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength | 15 | kJ/m2 | DIN EN ISO 179-1eU |
| Elongation at Break | 2 | % | DIN EN ISO 527-1 |
| Modulus of Elasticity (Tensile test) | 10500 | MPa | DIN EN ISO 527-1 |
| Tensile Strength | 86 | MPa | DIN EN ISO 527-1 |
Table 2 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Density | 1.51 | g/cm3 |
Table 3 of 5
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glass Transition Temperature | 143 | °C | — |
| Glass Transition Temperature | 264 | °C | ISO-R 75 Method A |
| Melting Temperature | 343 | °C | — |
| Service Temperature (long term) | 260 | °C | — |
| Service Temperature (short term) | 300 | °C | — |
| Specific Heat | 1.05 | J/(g*K) | DIN EN 821 |
| Thermal Conductivity (in-plane) | 5 | W/(K*m) | DIN EN 821 |
| Thermal Conductivity (through-plane) | 1.3 | W/(K*m) | DIN EN 821 |
| Thermal Diffusivity (in-plane) | 3.2 | mm2/s | DIN EN 821 |
| Thermal Diffusivity (through-plane) | 0.8 | mm2/s | DIN EN 821 |
| Thermal Expansion (CLTE) Longitudinal (at 200 - 260°C) | 51 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Thermal Expansion (CLTE) Longitudinal (at 23 - 100°C) | 16 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity | 6.3 x 10^7 | Ω | DIN EN 61340-2-3 |
| Volume Resistivity | 1.4 x 10^8 | Ω*cm | DIN EN 61340-2-3 |
Table 5 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bulk Density | 0.8 | g/cm3 | EN ISO 60 |
| Flammability (UL94 at 0.8mm and 1.6mm) | V0 | — | DIN IEC 60695-11-10 |
| Melt Flow Index (380°C / 10kg) | 21 | g/10 min | DIN EN ISO 1133 |
| Molding Shrinkage (longitudinal) | 0.48 | % | DIN EN ISO 294-4 |
| Molding Shrinkage (transverse) | 0.57 | % | DIN EN ISO 294-4 |
| Water Absorption (24h / 96h at 23°C / 50 %, relative humidity up to saturation) | 0.02 | % | DIN EN ISO 62 |