TECACOMP PA66 ID blue 4066
- Chemical Family
- Polyamides
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Housewares
Electrical & Electronics — Packaging & Assembly
- Other Packaging & Assembly Applications
Food & Nutrition — Processing & Packaging
- Food & Beverage Manufacturing
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- TECACOMP
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Other Filler
- Processing Methods
- Injection Molding
- Color
- Blue
- Markets
- Consumer Goods
- Electrical & Electronics
- Food & Nutrition
- Predrying
To achieve optimum mechanical properties, it is recommended to pre-dry the material w ith the above mentioned parameters.
- Technology
- Plastics
- Material Features
- Metal Detectable
- Processing Information
This material can be processed as a thermoplastic taking the normal technical provisions into account. The above mentioned information refers exclusively to the injection molding process.. Processing should be carried out as gently as possible, in order to maintain the maximum fiber length in the component. Back pressure and injection rate should be adjusted to the component geometry accordingly. The optimum processing temperature depends upon the respective geometry of the molded part and can be different from machine to machine.
- Certifications and Compliance
- FDA Compliant
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers End Uses
- Cable Ties
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bending Strain | 5.7 | % | DIN EN ISO 178 |
| Charpy Impact Strength | 113 | kJ/m2 | DIN EN ISO 179-1eU |
| Elongation at Break | 14.1 | % | DIN EN ISO 527-1 |
| Flexural Strength | 93 | MPa | DIN EN ISO 178 |
| Modulus of Elasticity (Flexural test) | 2600 | MPa | DIN EN ISO 178 |
| Modulus of Elasticity (Tensile test) | 3000 | MPa | DIN EN ISO 527-1 |
| Tensile Strength | 65 | MPa | DIN EN ISO 527-1 |
Table 2 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Glass Transition Temperature | 5 / 72 | °C |
| Melting Temperature | 260 | °C |
| Service Temperature (long term) | 110 | °C |
| Service Temperature (short term) | 170 | °C |
Table 3 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bulk Density | 0.72 | g/cm3 | EN ISO 60 |
| Detectability | 4.7 | mm Al | — |
| Flammability (UL94) | HB | — | DIN IEC 60695-11-10 |
| Melt Flow Index (280°C / 2.16 kg) | 20 | g/10 min | DIN EN ISO 1133 |
| Molding Shrinkage (longitudinal) | 2.06 | % | DIN EN ISO 294-4 |
| Molding Shrinkage (transverse) | 2.16 | % | DIN EN ISO 294-4 |
| Water Absorption (23°C / 50% relative humidity up to saturation) | 2.3 | % | DIN EN ISO 62 |