TECACOMP PEEK 450 PVX black 4247

Properties

Plastics — Engineering & Specialty Polymers

Brand: TECACOMP
Polymer Name: Polyetheretherketone (PEEK)
Processing Methods: Injection Molding
Color: Black
Predrying: To achieve optimum mechanical properties, it is recommended to pre-dry the material w ith the above mentioned parameters.
Technology: Plastics
Processing Information: This material can be processed as a thermoplastic taking the normal technical provisions into account. The above mentioned information refers exclusively to the injection molding process.. Processing should be carried out as gently as possible, in order to maintain the maximum fiber length in the component. Back pressure and injection rate should be adjusted to the component geometry accordingly. The optimum processing temperature depends upon the respective geometry of the molded part and can be different from machine to machine.
Plastics and Elastomers Processing Methods: Injection Molding

4 rows

Characteristic	Value	Unit	Method
Charpy Impact Strength	32	kJ/m2	DIN EN ISO 179-1eU
Elongation at Break (50 mm/min)	2.5	%	DIN EN ISO 527-1
Modulus of Elasticity (Tensile test, 50 mm/min)	10700	MPa	DIN EN ISO 527-1
Tensile Strength (50 mm/min)	140	MPa	DIN EN ISO 527-1

1 row

Characteristic	Value	Unit
Density	1.43	g/cm3

4 rows

Characteristic	Value	Unit	Method
Glass Transition Temperature	143	°C	DIN 53765
Melting Temperature	343	°C	DIN 53765
Service Temperature (long term)	260	°C	—
Service Temperature (short term)	300	°C	—

2 rows

Characteristic	Value	Unit	Method
Bulk Density	0.59	g/cm3	EN ISO 60
Melt Flow Index (380°C / 5kg)	2.5	g/10 min	DIN EN ISO 1133