TECACOMP PEEK 450 CF30 black 9579
- Chemical Family
- Polyether Ether Ketone (PEEK)
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Industrial — Other Industrial Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Industrial Automation
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- TECACOMP
- Polymer Name
- Polyetheretherketone (PEEK)
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- Predrying
To achieve optimum mechanical properties, it is recommended to pre-dry the material w ith the above mentioned parameters.
- Technology
- Plastics
- Material Features
- High Tensile Strength
- Processing Information
This material can be processed as a thermoplastic taking the normal technical provisions into account. The above mentioned information refers exclusively to the injection molding process.. Processing should be carried out as gently as possible, in order to maintain the maximum fiber length in the component. Back pressure and injection rate should be adjusted to the component geometry accordingly. The optimum processing temperature depends upon the respective geometry of the molded part and can be different from machine to machine.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength | 33 | kJ/m2 | DIN EN ISO 179-1eU |
| Elongation at Break (50 mm/min) | 1.5 | % | DIN EN ISO 527-1 |
| Modulus of Elasticity (Tensile test, 50 mm/min) | 22500 | MPa | DIN EN ISO 527-1 |
| Tensile Strength (50 mm/min) | 220 | MPa | DIN EN ISO 527-1 |
Table 2 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Density | 1.44 | g/cm3 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glass Transition Temperature | 143 | °C | DIN 53765 |
| Heat Distortion Temperature (HDTA) | 326 | °C | ISO-R 75 Method A |
| Melting Temperature | 343 | °C | DIN 53765 |
| Service Temperature (long term) | 260 | °C | — |
| Service Temperature (short term) | 300 | °C | — |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 2.41 x 10^2 | Ω*m | DIN EN ISO 3915 |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bulk Density | 0.63 | g/cm3 | EN ISO 60 |
| Melt Flow Index (380°C / 5kg) | 2.5 | g/10 min | DIN EN ISO 1133 |
| Molding Shrinkage (longitudinal) | 0.31 | % | DIN EN ISO 294-4 |
| Molding Shrinkage (transverse) | 0.89 | % | DIN EN ISO 294-4 |
| MVR (380°C / 5 kg) | 5.5 | cm3/10 min | DIN EN ISO 1133 |