Arnite® AV2 360 S
- Chemical Family
- Polyethylene Terephthalate (PET)
Arnite® AV2 360 S is a high-performance engineering plastic that combines high strength and rigidity with excellent processing characteristics. As a result, it is well suited for a broad range of automotive, electrical, electronics, and consumer goods applications. The processing technology is best suited for injection molding.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
Automotive & Transportation — Automotive
- Chassis & Brake
- Safety Systems
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Arnite
- Polymer Name
- Polyethylene Terephthalate (PET)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Quality Standards
- UL Yellow Card (E47960)
- Material Features
- Flame Retardant
- UL Flame Rated
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ISO 527-1/-2 |
| Stress at Break | 160 | MPa | ISO 527-1/-2 |
| Strain at Break | 2 | % | ISO 527-1/-2 |
| Charpy Impact Strength (at +23°C) | 35 | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | 35 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (at +23°C) | 8 | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 8 | kJ/m² | ISO 179/1eA |
Table 2 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 255 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.80 MPa) | 220 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 240 | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.2 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.65 | E-4/°C | ISO 11359-1/-2 |
| Burning Behaviour (at 1.5 mm Nominal Thickness) | UL V-0 | class | IEC 60695-11-10 |
| Burning Behaviour (at 3.0 mm Nominal Thickness) | UL V-0 | class | IEC 60695-11-10 |
| Oxygen Index | 36 | % | ISO 4589-1/-2 |
| Relative Temperature Index (Electrical, 0.71 mm) | 150 | °C | UL746B |
| Relative Temperature Index (Electrical, 3 mm) | 150 | °C | UL746B |
| Relative Temperature Index (with impact, 0.71 mm) | 125 | °C | UL746B |
| Relative Temperature Index (with impact, 3 mm) | 130 | °C | UL746B |
Table 3 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative Permittivity (100Hz) | 3.7 | — | IEC 62631-2-1 |
| Relative Permittivity (1 MHz) | 3.4 | — | IEC 62631-2-1 |
| Dissipation Factor (100 Hz) | 10 | E-4 | IEC 62631-2-1 |
| Dissipation Factor (1 MHz) | 120 | E-4 | IEC 62631-2-1 |
| Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
| Electric Strength | 29 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
Table 4 of 7
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Density of Melt | 1350 | kg/m³ |
| Thermal Conductivity of Melt | 0.195 | W/(m K) |
| Specific Heat Capacity Melt | 1670 | J/(kg K) |
| Effective Thermal Diffusivity | 8.67E-8 | m²/s |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 0.4 | % | Sim. to ISO 62 |
| Humidity Absorption | 0.12 | % | Sim. to ISO 62 |
| Density | 1730 | kg/m³ | ISO 1183 |
Table 6 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.5 | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1 | % | ISO 294-4 |
Химическая стойкость
215 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetic acid (10% by mass) at 23°C | resistant |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acrylic acid at 23°C | resistant |
| Other | Aliphatic amines at 23°C | resistant |
| Other | Aliphatic hydrocarbons at 23°C | resistant |
| Other | Alkylbenzenes at 23°C | resistant |
| Other | Allyl alcohol at 23°C | resistant |
| Other | Aluminum hydroxide (saturated) at 23°C | resistant |
| Other | Aluminum salts of mineral acids (saturated) at 23°C | resistant |
| Other | Ammonia at 23°C | limited resistant, tests necessary to verify |