Stanyl® TW271B3
- Chemical Family
- Polyamides
Stanyl® TW271B3 is a high-performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear and friction, and process flow qualities are required. This high-performance polyamide 46 is used for applications in automotive, E&E, gears, and outdoor power equipment. Since it retains its mechanical properties at high temperatures up to 220 °C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP. A suitable processing technology for the product is injection molding. Special features include being heat stabilized, wear modified, and friction modified.
Product families
- Polyamides
Other characteristics
- Brand
- Stanyl
- Polymer Name
- Polyamide 46 (PA 46)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 12000.0 - 12000.0 MPa
- Additives Included
- Heat Stabilizer, Lubricant (PTFE)
- Heat Stabilizer
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- OEM Standards
- General Motors
- PSA
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Quality Standards
- UL Yellow Card (E172082)
- Material Features
- Friction Resistant
- Heat Resistance
- Heat Stabilized
- Low Friction
- Low Wear
- UL Flame Rated
- Wear Resistant
- OEM Specifications
- GM GMW15702-110041
- PSA Peugeot-Citroen FTM 64 0115
- Gears Application Data
Broad portfolio of high-performance polyamide materials for gears; Stanyl® PA46 grades consistently proven to outperform PA66 and POM; Stanyl® offers comparable but less expensive performance thank PEEK; High-performance Stanyl® grades enable more compact design and lightweighting opportunities; Advanced bio-based EcoPaXX® PA410 grades also available for a great combination of performance and sustainability
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- UL 94
- Plastics and Elastomers End Uses
- Actuators
- Automotive Electronics
- Automotive Gears
- Bearing Cages
Technical data
Table 1 of 6
30 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 13500 / 6700 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 13500 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 6300 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 5700 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 5400 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 5100 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 195 / 120 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 230 / - | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 108 / - | MPa | ISO 527-1/-2 |
| Stress at Break (160°C) | 92 / * | MPa | ISO 527-1/-2 |
| Stress at Break (180°C) | 84 / * | MPa | ISO 527-1/-2 |
| Stress at Break (200°C) | 76 / * | MPa | ISO 527-1/-2 |
Table 2 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 295 / * | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | 75 / * | °C | ISO 11357-1/-2 |
| Temperature of Deflection Under Load (1.80 MPa) | 290 / * | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.25 / * | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.5 / * | E-4/°C | ISO 11359-1/-2 |
| Burning Behaviour (at 3 / * mm Nominal Thickness) | UL HB / * | class | IEC 60695-11-10 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 1E5 / - | Ohm*m | IEC 62631-3-1 |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 9.5 / * | % | Sim. to ISO 62 |
| Water Absorption in Water (at 23°C after 24h) | 2.65 / * | % | ISO 62 |
| Humidity Absorption | 2.6 / * | % | Sim. to ISO 62 |
| Density | 1320 / - | kg/m³ | ISO 1183 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.2 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 0.8 / * | % | ISO 294-4 |
Химическая стойкость
377 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | not resistant |
| Other | Acetic acid (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | not resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Acrylic acid at 23°C | not resistant |
| Other | Aliphatic amines at 23°C | resistant |