Stanyl® TW241B3
- Chemical Family
- Polyamides
Stanyl® TW241B3 is a high-performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear and friction, and process flow qualities are required. This high-performance polyamide 46 is used for applications in automotive, E&E, gears, and outdoor power equipment. Since it retains its mechanical properties at high temperatures up to 220 °C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP. A suitable processing technology for the product is injection molding. Special features include being heated, stabilized, and lubricated.
Product families
- Polyamides
Other characteristics
- Brand
- Stanyl
- Polymer Name
- Polyamide 46 (PA 46)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 11500.0 - 11500.0 MPa
- Additives Included
- Heat Stabilizer, Lubricant (Unspecified)
- Heat Stabilizer
- Lubricant (Unspecified)
- Processing Methods
- Injection Molding
- Safety
For the safety properties of the material, we refer to our SDS which can be ordered at our sales offices. During practical operation we advise to wear personal safety protections for hand/eye/body.
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Cost Effective
- Heat Resistance
- Heat Stabilized
- Light Weight
- Lubricated
- Gears Application Data
Broad portfolio of high-performance polyamide materials for gears; Stanyl® PA46 grades consistently proven to outperform PA66 and POM; Stanyl® offers comparable but less expensive performance thank PEEK; High-performance Stanyl® grades enable more compact design and lightweighting opportunities; Advanced bio-based EcoPaXX® PA410 grades also available for a great combination of performance and sustainability
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Power Seats Application Data
Stanyl® PA46 allows for lightweight and cost effective solutions as compared to machined cast metal and also offers advantages in NVH; Stanyl® PA46 allows for reliable solutions due to its superiority in temperature and abrasion performance as compared to PA66 and POM; Stanyl® PA46 allows for cost effective solutions due to its faster cycle times in comparison with PA66 and PPA
- Plastics and Elastomers End Uses
- Actuators
- Automotive Electronics
- Automotive Gears
- Power Seats
Technical data
Table 1 of 6
32 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 13000 / 7000 | MPa | ISO 527-1/-2 |
| Tensile Modulus (-40°C) | 13000 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 6800 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (160°C) | 6400 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (180°C) | 6100 / * | MPa | ISO 527-1/-2 |
| Tensile Modulus (200°C) | 5200 / * | MPa | ISO 527-1/-2 |
| Stress at Break | 210 / 130 | MPa | ISO 527-1/-2 |
| Stress at Break (-40°C) | 250 / - | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 100 / - | MPa | ISO 527-1/-2 |
| Stress at Break (160°C) | 87 / * | MPa | ISO 527-1/-2 |
| Stress at Break (180°C) | 81 / * | MPa | ISO 527-1/-2 |
| Stress at Break (200°C) | 75 / * | MPa | ISO 527-1/-2 |
Table 2 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 295 / * | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | 75 / * | °C | ISO 11357-1/-2 |
| Temperature of Deflection Under Load (1.80 MPa) | 290 / * | °C | ISO 75-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 0.25 / * | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 0.5 / * | E-4/°C | ISO 11359-1/-2 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 1E5 / - | Ohm*m | IEC 62631-3-1 |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 11.5 / * | % | Sim. to ISO 62 |
| Water Absorption in Water (at 23°C after 24h) | 3.2 / * | % | ISO 62 |
| Humidity Absorption | 3.2 / * | % | Sim. to ISO 62 |
| Density | 1230 / - | kg/m³ | ISO 1183 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding Shrinkage (parallel) | 0.3 / * | % | ISO 294-4 |
| Molding Shrinkage (normal) | 1.1 / * | % | ISO 294-4 |
Химическая стойкость
377 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | not resistant |
| Other | Acetic acid (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | not resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Acrylic acid at 23°C | not resistant |
| Other | Aliphatic amines at 23°C | resistant |