Stanyl® HFX63S

Chemical Family: Polyamides

Stanyl® HFX63S is a high-performance polyamide 46 used for applications in automotive, E&E, gears, and outdoor power equipment. It is a high-performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear and friction, and process flow qualities are required. Since it retains its mechanical properties at high temperatures up to 220 °C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP. A suitable processing technology for the product is injection molding. Special features include good or high flow and being phosphorous-free.

Product families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: Stanyl
Polymer Name: Polyamide 46 (PA 46)
Fillers Included: Glass Fiber
Flexural Modulus: 10500.0 - 10500.0 MPa
Additives Included: Flame Retardant
Processing Methods: Injection Molding
Technology: Plastics
Labeling Claims: Halogen-free
Phosphorus-free
Special Features: 35% Glass Reinforced
Good or high flow
Phosphorous free
Halogen free
Quality Standards: UL Yellow Card (E47960)
Material Features: Flame Retardant
High Flow

Technical data

Table 1 of 5

13 rows

Characteristic	Value	Unit	Method
Tensile Modulus	12300 / 8600	MPa	ISO 527-1/-2
Tensile Modulus (at 120°C)	6600 / -	MPa	ISO 527-1/-2
Tensile Modulus (at 160°C)	5700.0	MPa	ISO 527-1/-2
Stress at Break	150 / 110	MPa	ISO 527-1/-2
Stress at Break (at 120°C)	89 / -	MPa	ISO 527-1/-2
Stress at Break (at 160°C)	70.0	MPa	ISO 527-1/-2
Strain at Break	2.5 / 3.5	%	ISO 527-1/-2
Strain at Break (at 120°C)	4.5 / -	%	ISO 527-1/-2
Strain at Break (at 160°C)	5.0	%	ISO 527-1/-2
Flexural Modulus	10500 / 8000	MPa	ISO 178
Flexural Strength	210 / 200	MPa	ISO 178
Charpy Impact Strength (at 23°C)	50 / 60	kJ/m²	ISO 179/1eU

Table 2 of 5

3 rows

Characteristic	Value	Unit	Method
Melting Temperature (10°C/min)	295 / *	°C	ISO 11357-1/-3
Burning Behaviour (at 1.5 mm Nominal Thickness)	V-0 / *	Class	IEC 60695-11-10
Thickness Tested	1.5 / *	mm	IEC 60695-11-10

Table 3 of 5

7 rows

Characteristic	Value	Unit	Method
Volume Resistivity	min. 1E13 / 1E11	Ohm*m	IEC 62631-3-1
Electric Strength	30 / -	kV/mm	IEC 60243-1
Comparative Tracking Index	550 / -	V	IEC 60112
Relative Permittivity (at 100Hz)	4.4 / -	—	IEC 62631-2-1
Relative Permittivity (at 1 MHz)	4.1 / -	—	IEC 62631-2-1
Relative Permittivity (at 1GHz)	3.9 / -	—	IEC 61189-2-721
Relative Permittivity (at 10GHz)	3.8 / -	—	IEC 61189-2-721

Table 4 of 5

2 rows

Characteristic	Value	Unit	Method
Humidity Absorption	2.1 / *	%	Sim. to ISO 62
Density	1510 / -	kg/m³	ISO 1183