Stanyl® TW213F2 is a high-performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear and friction, and process flow qualities are required. This high-performance polyamide 46 is used for applications in automotive, E&E, gears, and outdoor power equipment. Since it retains its mechanical properties at high temperatures up to 220 °C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP. A suitable processing technology for the product is injection molding. Special features include heat stabilization.
Product families
Applications
- Sensors & Actuators
Product Families
- Polyamides
Other characteristics
- Brand
- Stanyl
- Polymer Name
- Polyamide 46 (PA 46)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Safety
For the safety properties of the material, we refer to our SDS which can be ordered at our sales offices. During practical operation we advise to wear personal safety protections for hand/eye/body.
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Packaging Type
- Bags
- Boxes
- Silos
- Super Sacks
- Material Features
- Heat Resistance
- Heat Stabilized
- Impact Modified
- Certifications and Compliance
- ISO 14001
- OHSAS
- REACH (Europe)
- Packaging for Injection Molding
Stanyl® grades are supplied in airtight, moisture-proof packaging.
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 3700 / - | MPa | ISO 527-1/-2 |
| Tensile Modulus (120°C) | 1400 / - | MPa | ISO 527-1/-2 |
| Stress at Break | 95 / - | MPa | ISO 527-1/-2 |
| Stress at Break (120°C) | 50 / - | MPa | ISO 527-1/-2 |
| Strain at Break | 10 / - | % | ISO 527-1/-2 |
| Strain at Break (at 120°C) | 24 / - | % | ISO 527-1/-2 |
| Charpy Notched Impact Strength (at +23°C) | 12 / - | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 5 / - | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at +23°C) | 12 / - | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (at -40°C) | 5 / - | kJ/m² | ISO 180/1A |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 295 / * | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | 75 / * | °C | ISO 11357-1/-2 |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 11.5 / * | % | Sim. to ISO 62 |
| Water Absorption in Water (at 23°C after 24h) | 3.1 / * | % | ISO 62 |
| Humidity Absorption | 3 / * | % | Sim. to ISO 62 |
| Density | 1180 / - | kg/m³ | ISO 1183 |
Химическая стойкость
377 rows| Characteristic | Value | Unit |
|---|---|---|
| Other | Acetaldehyde (40% by mass) at 23°C | resistant |
| Other | Acetamide (50% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetamide (50% by mass) at >140°C | not resistant |
| Other | Acetic acid (10% by mass) at 100°C | not resistant |
| Other | Acetic acid (10% by mass) at 23°C | limited resistant, tests necessary to verify |
| Other | Acetic acid (95% by mass) at 23°C | not resistant |
| Ketones | Acetone at 23°C | resistant |
| Other | Acetophenone at 23°C | resistant |
| Other | Acetyl chloride at 23°C | not resistant |
| Other | Acetylene at 23°C | resistant |
| Other | Acrylic acid at 23°C | not resistant |
| Other | Aliphatic amines at 23°C | resistant |