Stanyl® TE200F6-FC

Chemical Family: Polyamides

Stanyl® TE200F6-FC is a high-performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear and friction, and process flow qualities are required. This high-performance polyamide 46 is used for applications in automotive, E&E, gears, and outdoor power equipment. Since it retains its mechanical properties at high temperatures up to 220 °C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP. A suitable processing technology for the product is injection molding. Special features include heat stabilization.

Product families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: Stanyl
Polymer Name: Polyamide 46 (PA 46)
Fillers Included: Glass Fiber
Flexural Modulus: 9500.0 - 9500.0 MPa
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Safety: For the safety properties of the material, we refer to our SDS which can be ordered at our sales offices. During practical operation we advise to wear personal safety protections for hand/eye/body.
Markets: Building & Construction
Consumer Goods
Industrial
Flame Rating: UL 94 HB
Technology: Plastics
Packaging Type: Bags
Boxes
Silos
Super Sacks
Labeling Claims: Food Contact Acceptable
Quality Standards: UL Yellow Card (E47960)
Material Features: Food Contact Acceptable
Heat Resistance
Heat Stabilized
UL Flame Rated
Panhandle Application Data: High use temperature
Non-stick and easy to clean
Passes food contact regulation
Low oligomer content vs PA66
Certifications and Compliance: ISO 14001
OHSAS
REACH (Europe)
UL 94
Pipe Fittings Application Data: Akulon® PA6 allows for reliable solutions due to its good mechanical properties (stiff and tough) and its better surface appearance than PA66; Stanyl® PA46 allows for more economical and reliable solutions than PES or PPSU also as a result of a very good creep resistance at elevated temperatures; Xytron™ PPS can provide super hydrolysis.
Plastics and Elastomers End Uses: Appliances
Cookware Handles
Fittings
Garden Equipment
Kitchenware
Lawn Equipment
Pipes
Plastics and Elastomers Functions: Resin

Technical data

Table 1 of 8

38 rows

Characteristic	Value	Unit	Method
Tensile Modulus	10000 / 6000	MPa	ISO 527-1/-2
Tensile Modulus (-40°C)	10200 / -	MPa	ISO 527-1/-2
Tensile Modulus (120°C)	5300 / -	MPa	ISO 527-1/-2
Tensile Modulus (160°C)	4750 / *	MPa	ISO 527-1/-2
Tensile Modulus (180°C)	4550 / *	MPa	ISO 527-1/-2
Tensile Modulus (200°C)	4300 / *	MPa	ISO 527-1/-2
Tensile Modulus (Low Thickness, 1mm) - Dry	10000	MPa	ISO 527-1/-2
Tensile Modulus (Low Thickness) - cond.	6000	MPa	ISO 527-1/-2
Stress at Break	210 / 115	MPa	ISO 527-1/-2
Stress at Break (-40°C)	250 / -	MPa	ISO 527-1/-2
Stress at Break (120°C)	115 / -	MPa	ISO 527-1/-2
Stress at Break (160°C)	100 / *	MPa	ISO 527-1/-2

Table 2 of 8

18 rows

Characteristic	Value	Unit	Method
Melting Temperature (10°C/min)	295 / *	°C	ISO 11357-1/-3
Glass Transition Temperature (at 10°C/min)	75 / *	°C	ISO 11357-1/-2
Temperature of Deflection Under Load (1.80 MPa)	290 / *	°C	ISO 75-1/-2
Temperature of Deflection Under Load (0.45 MPa)	290 / *	°C	ISO 75-1/-2
Vicat Softening Temperature (50°C/h 50N)	290 / *	°C	ISO 306
Coefficient of Linear Thermal Expansion (parallel)	0.25 / *	E-4/°C	ISO 11359-1/-2
Coefficient of Linear Thermal Expansion (normal)	0.6 / *	E-4/°C	ISO 11359-1/-2
Burning Behaviour (at 1.5 mm Nominal Thickness)	UL HB / *	class	IEC 60695-11-10
Burning Behaviour (at 3.0 mm Nominal Thickness)	UL HB / *	class	IEC 60695-11-10
Oxygen Index	22 / *	%	ISO 4589-1/-2
Glow Wire Flammability Index (at thickness 3 / - mm)	925 / -	°C	IEC 60695-2-12
Glow Wire Flammability Index (at thickness 0.75 / - mm)	675 / -	°C	IEC 60695-2-12

Table 3 of 8

10 rows

Characteristic	Value	Unit	Method
Relative Permittivity (100Hz)	4.4 / 12	—	IEC 62631-2-1
Relative Permittivity (1 MHz)	4 / 4.6	—	IEC 62631-2-1
Relative Permittivity (1GHz)	3.6 / -	—	IEC 60250
Dissipation Factor (100 Hz)	80 / 1500	E-4	IEC 62631-2-1
Dissipation Factor (1 MHz)	230 / 900	E-4	IEC 62631-2-1
Dissipation Factor (1GHz)	300 / -	E-4	IEC 60250
Volume Resistivity	1E13 / 1E9	Ohm*m	IEC 62631-3-1
Surface Resistivity	- / 1E14	Ohm	IEC 62631-3-2
Electric Strength	35 / 25	kV/mm	IEC 60243-1
Comparative Tracking Index	500 / -	V	IEC 60112

Table 4 of 8

1 row

Characteristic	Value	Unit	Method
Viscosity Number	145 / *	cm³/g	ISO 307, 1157, 1628

Table 5 of 8

4 rows

Characteristic	Value	Unit
Density of Melt	1280 / *	kg/m³
Thermal Conductivity of Melt	0.28 / *	W/(m K)
Specific Heat Capacity Melt	2430 / *	J/(kg K)
Effective Thermal Diffusivity	9.02E-8 / *	m²/s

Table 6 of 8